| Hot deformation behavior and processing map of low-alloy offshore steel |
| Shi-ping Xi1, Xin-liang Gao1, Wei Liu1, Yan-lu Lu1, Gui-qin Fu2, Hui-cheng Tao1, Yong-chang Zang1 |
1 National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, College of Mechanical Engineering, Yanshan University, Qinhuangdao 066004, Hebei, China
2 College of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
|
|
Abstract The hot deformation behavior of a low-alloy offshore steel was systematically investigated within the temperature range of 850–1150 °C and strain rate range of 0.01–10 s–1, via hot compression testing. The hot working equation, grain size model and recrystallization kinetic models of the steel were developed by fitting the experimental data. The results show that the decrease in Zener–Hollomon Z-parameter value (the increase in deformation temperature and the decrease in strain rate) is beneficial for the occurrence of dynamic recrystallization, and the grain size can be refined by increasing the Z-parameter value within the deformation range of dynamic recrystallization. However, when the Z-parameter value is higher than 3.43 × 1016, dynamic recrystallization will be difficult to occur within the range of experimental deformation conditions. Additionally, processing maps at different strains were constructed. According to the processing map and microstructural analysis, the optimal hot working conditions of the studied steel are within the temperature range of 1000–1100 °C and strain rate range of 0.1–1 s-1, and a complete recrystallization microstructure with fine homogeneous grains could be obtained.
|
|
Received: 02 December 2020
Published: 25 March 2022
|
|
|
|
| Cite this article: |
|
Shi-ping Xi,Xin-liang Gao,Wei Liu, et al. Hot deformation behavior and processing map of low-alloy offshore steel[J]. Journal of Iron and Steel Research International, 2022, 29(3): 474-483.
|
|
|
|
| [1] |
Xin-pan Yu, Hui-bin Wu, Yang Gu, Rui Yuan, You-you Zhang, Yu-hui Feng. Effect of prior martensite on bainite transformation and microstructure of high-carbon nano-bainitic steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(4): 647-654. |
| [2] |
Run-feng Peng, Min Zhang, Yu-hang Li, Yue-long Yu, Ying-chun Guan, Zhun-li Tan. Microstructural development and wear properties analyses of Febased coatings on bainitic steel by laser cladding[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(4): 687-697. |
| [3] |
Zhi-xiang Fu, Geng-wei Yang, Ru-yang Han, Yao-wen Xu, Xin-ping Mao, Si-qian Bao, Gang Zhao. Influence of coiling temperature on microstructure and mechanical properties of a hot-rolled high-strength steel microalloyed with Ti, Mo and V[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(3): 484-493. |
| [4] |
Li-ying Liu, Ping Yang, Dan-dan Ma, Xin-fu Gu. Surface effect induced phase transformation by Mn removal during annealing and its textures in cold-rolled high manganese transformation-induced plasticity steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(3): 494-502. |
| [5] |
Guang-hui Zhao, Jian Zhang, Juan Li, Hua-ying Li, Hai-tao Liu, Li-feng Ma. Effect of copper on edge cracking behavior and microstructure of rolled austenitic stainless steel plate[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(2): 281-294. |
| [6] |
Fan Zhao, Guo-ning He, Ya-zheng Liu, Zhi-hao Zhang, Jian-xin Xie. Effect of titanium microalloying on microstructure and mechanical properties of vanadium microalloyed steels for hot forging[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(2): 295-306. |
|
|
|
|
2022, Vol. 29 