| Influence of Cr2O3 content on viscosity and rheological behavior of Cr2O3-containing slags |
| Fang Yuan1, Zheng Zhao1, Yan-ling Zhang1, Tuo Wu1 |
| 1 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract The rheological behavior of Cr2O3-containing slags was investigated using a rotating cylinder viscometer and the solid fraction and phases of Cr2O3 in molten slags were also calculated and observed at different temperatures. Furthermore, the viscosities of CaO–SiO2–Cr2O3(–10%Al2O3) slags were measured from 1703 to 1953 K and the influence of Cr2O3 content on the viscosity and rheological behavior of molten slags was investigated. The calculation revealed that the solid fraction of the molten slags varied with the Cr2O3 content and maximum temperature, and the fluid properties transitioned from Newtonian to non-Newtonian behavior when the solid fraction reached 5%. Moreover, the increase in Cr2O3 content led to an increase in the viscosity as the slags displayed Newtonian flow characteristics and a decrease in the viscosity when slags exhibited non-Newtonian flow characteristics. The viscosity results of Cr2O3-containing slag from 1703 to 1953 K and from 1703 to 1813 K were also discussed with the morphologies.
|
|
|
|
|
|
| Cite this article: |
|
Fang Yuan,Zheng Zhao,Yan-ling Zhang, et al. Influence of Cr2O3 content on viscosity and rheological behavior of Cr2O3-containing slags[J]. Journal of Iron and Steel Research International, 2022, 29(4): 601-611.
|
|
|
|
| [1] |
Xin-bo Ji, Si-xin Zhao, Li-ming Fu, Jian Peng, Jia-qiang Gao, Da-jiang Yu, Zong-ze Huang, Ai-dang Shan. High cycle rotating bending fatigue performance and fracture behavior in a pearlite–ferrite dual-phase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(3): 519-528. |
| [2] |
Le-jun Zhou, Hao Luo, Wan-lin Wang, Xiong Yan, Hou-fa Wu. Effect of Al2O3/Na2O ratio and MnO on high-temperature properties of mold flux for casting peritectic steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(01): 53-60. |
| [3] |
Yang Chen, Sheng-ping He, Zhi-rong Li, Xu-bin Zhang, Qiang-qiang Wang, Qian Wang. Properties and structure of a new non-reactive mold flux for high-Al steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(01): 61-70. |
| [4] |
Jing‑jing Pei, Jin‑hu Wu, Wen‑qing Huo, Yu‑zhu Zhang, Hong‑wei Xing, Qian‑qian Ren. Structure characterization and grinding performance of gas-quenched steel slag abrasive[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(4): 383-390. |
| [5] |
Guang-zong Zhang, Nan Wang, Min Chen, Yan-qing Cheng. Viscosity prediction on iron-bearing slags during pyrometallurgical recycling: structure-based modeling of CaO2-‘FeO’-2MgO-2Al2O3-2SiO2 system and its subsystems[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(06): 679-692. |
| [6] |
Qian Zhang, Da Ren, Zhi-pu Liu, Chen-chong Wang, Jian Huang, Wei Xu. Composition and processing of direct-quench hot rolled steels with ultrahigh strength exceeding GPa[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(06): 703-712. |
|
|
|
|
2022, Vol. 29 