| Evaluation of increasing service life of epoxy zinc-rich coating on 3 wt.% Ni-advanced low-alloy steel in marine atmospheric environment |
| Sheng-rong Wang1,2, Jian-wei Yang1,2, Jian-ping Cao1,2, Shan Jiang1,2, Fei-fan Xu1,2 |
| 1 Shougang Research Institute of Technology of Shougang Group Co., Ltd., Beijing 100043, China 2 Beijing Key Laboratory of Green Recyclable Process for Iron & Steel Production Technology, Beijing 100043, China |
|
|
|
|
Abstract The addition of Ni element into steel to prolong the service life of coated steel was investigated in marine atmospheric environment by laboratory simulated accelerated experiment. The scanning electron microscope and electron probe microanalysis combined with electrochemical impedance spectroscopy were used to characterize coated steel properties and examined the anti-corrosion performance. The results showed that 3 wt.% Ni-advanced steel (3Ni steel) substrate obviously delayed the failure time of coating compared to carbon steel, therefore prolonging the service life of coating on the steel. X-ray diffraction patterns for the corrosion products under the scratched coating on 3Ni steel exhibited that FeNi2O4 and Fe2O3 occurred in the corrosion product of 3Ni steel. It was also found that Ni element enriched in the product layer through analyzing the appearance and composition of corrosion products by electron probe micro-analysis. Chloride ions were blocked out of product by the enrichment of Ni element in rust layer.
|
|
Received: 14 April 2022
|
|
|
|
| Cite this article: |
|
Sheng-rong Wang,Jian-wei Yang,Jian-ping Cao, et al. Evaluation of increasing service life of epoxy zinc-rich coating on 3 wt.% Ni-advanced low-alloy steel in marine atmospheric environment[J]. Journal of Iron and Steel Research International, 2022, 29(4): 698-706.
|
|
|
|
| [1] |
Mao-fang Zuo, Yin-li Chen, Zhen-li Mi, Yi-de Wang, Hai-tao Jiang. Effects of Cr content on corrosion behaviour and corrosion products of spring steels[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(9): 1000-1010. |
| [2] |
Jian Li . Hang Su . Feng Chai . Dong-mei Xue . Li Li . Xiang-yang Li . Hui-min Meng. Corrosion behavior of low-carbon Cr micro-alloyed steel for grounding grids in simulated acidic soil[J]. , 2018, 25(7): 755-765. |
| [3] |
LI Ming,SHI Zhi-min,LIU Yu-bao. Crevice Corrosion of K60 in Dry Desertification Saline Soil[J]. Chinese Journal of Iron and Steel, 2013, 20(4): 76-80. |
| [4] |
XIAO Kui;DONG Chaofang;LI Xiaogang;WANG Fuming. Corrosion Products and Formation Mechanism During Initial Stage of Atmospheric Corrosion of Carbon Steel[J]. Chinese Journal of Iron and Steel, 2008, 15(5): 42-0. |
| [5] |
LIN Guanfa;ZHENG Maosheng;BAI Zhenquan;FENG Yaorong. Wear Resistance of CO2 Corrosion Product Scale Formed at High Temperature[J]. Chinese Journal of Iron and Steel, 2006, 13(5): 0-47. |
|
|
|
|
2022, Vol. 29 