| Achieving efficient utilization of limonitic nickel laterite and CO2 emission reduction through multi-force field sintering process |
| Yu-xiao Xue1, De-qing Zhu1, Zheng-qi Guo1, Jian Pan1, Yi-ge Wang1, Qing-zhou Huang2, Liao-ting Pan2, Xue-zhong Huang2 |
| 1 School of Minerals Processing and Bioengineering, Central South University, Changsha 410083, Hunan, China 2 Guangxi Beibu Gulf New Materials Co., Ltd., Beihai 536000, Guangxi, China |
|
|
|
|
Abstract Strengthening limonitic nickel laterite sintering and reducing CO2 emission were performed by the application of multiforce fields including external thermodynamic and pressure fields. Sinter pot tests of limonitic nickel laterite were carried out, and the relevant industrial production was briefed. The chemistry and mineralogy of product sinter and the thermodynamic and kinetic conditions during sintering were analyzed to reveal the relevant mechanism. The results indicate that sintering performance of limonitic nickel laterite in the new sintering process with multi-force fields is significantly improved with tumble index and productivity increased by 24.11% and 18.56%, respectively, and solid fuel rate reduced by 23.21%, compared with those in traditional sintering process. In this case, greenhouse and pollutant gas emissions are greatly reduced, and metallurgical performances of product sinter are excellent. The industrial production has been successfully conducted, indicating a bright application prospect. Mechanism analysis shows that the great improvement of thermodynamic and kinetic conditions during sintering and the densification of loose sinter can be achieved via the application of multi-force fields. Sinter microstructure is transformed from large thin-wall pores to small thin-wall pores or medium thick-wall pores with the dramatic reduction of sinter porosity and more formation of silico-ferrite of calcium and alumina (SFCA). Meanwhile, the homogenization of mineral compositions is achieved, and much denser interlocking texture between hercynite and SFCA is formed. The application of multi-force fields contributes to the substantial improvement of sintering performance of limonitic nickel laterite and CO2 emission reduction.
|
|
|
|
|
|
| Cite this article: |
|
Yu-xiao Xue,De-qing Zhu,Zheng-qi Guo, et al. Achieving efficient utilization of limonitic nickel laterite and CO2 emission reduction through multi-force field sintering process[J]. Journal of Iron and Steel Research International, 2022, 29(11): 1734-1747.
|
|
|
|
| [1] |
Yu-xiao Xue, De-qing Zhu, Jian Pan, Zheng-qi Guo, Hong-yu Tian, Gen Li, Qing-zhou Huang, Liao-ting Pan, Xue-zhong Huang. Significant influence of self-possessed moisture of limonitic nickel laterite on sintering performance and its action mechanism[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(09): 1368-1380. |
|
|
|
|
2022, Vol. 29 