| Effects of MgO/Al2O3 and CaO/SiO2 ratios on viscosity of high titaniumbearing blast furnace slag |
| Hua-bin Gao1, Jue Tang1,2, Man-sheng Chu3, Shu-yu Zhong1, Zheng-gen Liu1 |
| 1 School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China; 2 Liaoning Province Engineering Research Center for Technologies of Low-Carbon Steelmaking, Northeastern University, Shenyang 110819, Liaoning, China; 3 State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
|
|
Abstract The effects of MgO/Al2O3 and CaO/SiO2 ratios on the viscosity, break-point temperature, and viscous activation energy of a high titanium-bearing slag were studied. The results showed that both the viscosity and the break-point temperature of the slag decreased with the MgO/Al2O3 ratio increasing from 0.50 to 0.65, the viscous activation energy decreased gradually, and the thermal stability became better. In addition, with an increase in CaO/SiO2 ratio from 1.12 to 1.22, the main viscous units in the slag depolymerized and the viscosity of slag decreased. However, the break-point temperature of slag showed an increasing tendency. The viscous activation energy decreased gradually and the thermal stability became better. The basic phase in the experimental high titanium-bearing slag was pyroxene, and its amount increased with increasing the MgO/Al2O3 ratio while decreased with increasing the CaO/SiO2 ratio.
|
|
|
|
|
|
| Cite this article: |
|
Hua-bin Gao,Jue Tang,Man-sheng Chu, et al. Effects of MgO/Al2O3 and CaO/SiO2 ratios on viscosity of high titaniumbearing blast furnace slag[J]. Journal of Iron and Steel Research International, 2023, 30(03): 456-464.
|
|
|
|
| [1] |
Ding-li Zheng, Guo-jun Ma, Xiang Zhang, Meng-ke Liu, Ju Xu. Effect of CaO/Al2O3 on structure, viscosity, and surface tension of electroslag remelting-type CeO2-bearing slag[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(4): 717-725. |
| [2] |
Fu-bin Liu, Jun-zhe Gao, Hai-bo Cao, Hua-bing Li, Zhou-hua Jiang, Xin Geng, Cong-peng Kang, Kui Chen, Rui-dong An. Effect of slag composition on elements oxidation behavior of GH984G superalloy for electroslag remelting withdrawal process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(5): 761-771. |
| [3] |
Fang Yuan, Zheng Zhao, Yan-ling Zhang, Tuo Wu. Influence of Cr2O3 content on viscosity and rheological behavior of Cr2O3-containing slags[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(4): 601-611. |
| [4] |
Le-jun Zhou, Hao Luo, Wan-lin Wang, Xiong Yan, Hou-fa Wu. Effect of Al2O3/Na2O ratio and MnO on high-temperature properties of mold flux for casting peritectic steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(01): 53-60. |
| [5] |
Yang Chen, Sheng-ping He, Zhi-rong Li, Xu-bin Zhang, Qiang-qiang Wang, Qian Wang. Properties and structure of a new non-reactive mold flux for high-Al steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(01): 61-70. |
| [6] |
Guang-zong Zhang, Nan Wang, Min Chen, Yan-qing Cheng. Viscosity prediction on iron-bearing slags during pyrometallurgical recycling: structure-based modeling of CaO2-‘FeO’-2MgO-2Al2O3-2SiO2 system and its subsystems[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(06): 679-692. |
|
|
|
|
2023, Vol. 30 