| Numerical investigation on melting characteristics of scrap with heat and mass transfers in molten steel |
| Cong-lin Yao1, Hong-chun Zhu1,2,3, Zhou-hua Jiang1,4,5, Hua-bing Li1,2,3,4,5, Hong-bin Lu1, Shu-cai Zhang1,2,3, Hao Feng1,2,3 |
| 1 School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China; 2 Institute for Frontier Technologies of Low-Carbon Steelmaking, Northeastern University, Shenyang 110819, Liaoning, China; 3 Liaoning Province Engineering Research Center for Technologies of Low-Carbon Steelmaking, Northeastern University, Shenyang 110819, Liaoning, China; 4 State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, Liaoning, China; 5 Key Laboratory for Ecological Metallurgy of Multimetallic Ores (Ministry of Education), Shenyang 110819, Liaoning, China |
|
|
|
|
Abstract Herein, a numerical simulation with simultaneous heat and mass transfers is carried out to investigate the scrap melting characteristics in molten steel after model verification by published experimental data. The numerical results show that the scrap melting stages consist of the frozen shell formation stage, the frozen shell remelting stage and the parent scrap melting stage. The heat transfer coefficient and the carbon mass transfer coefficient between the scrap and the molten steel are, respectively, in the range of 4209–6249 W m-2 K-1 and 6.4 × 10–5 m s-1. Meanwhile, the effects of process parameters on scrap melting time were studied. An increase in the scrap preheating temperature (Tscrap ), the molten steel temperature (Tsteel )and the carbon content of molten steel (Csteel) , and a decrease in the scrap thickness dscrap , can reduce the frozen shell existence time, as well as the scrap melting time. On this basis, a quantitative relationship between the aforementioned process parameters and the scrap melting time is obtained to predict the formation of frozen shell (W), which provides process guidance for shortening the scrap melting time. The quantitative relationship is expressed as: lnΨ=311.32-2.34lnTscrap -39.99lnTsteel -0.08lndscrap-0.57lnCsteel.
|
|
|
|
|
|
| Cite this article: |
|
Cong-lin Yao,Hong-chun Zhu,Zhou-hua Jiang, et al. Numerical investigation on melting characteristics of scrap with heat and mass transfers in molten steel[J]. Journal of Iron and Steel Research International, 2023, 30(6): 1090-1100.
|
|
|
|
| [1] |
Ming-ming Li, Zhen-qiang Wu, Lin Li, Zong-shu Zou. Numerical simulation of Marangoni effect induced by species transfer across iron droplet–molten slag interface[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(6): 1109-1116. |
| [2] |
Chao Lv, Xu-xin Chen, Zhao-xiang Ji, Hong-liang Zhao, Tao Yang, Lin-hui Yu. Simulation of bubble breaking process in a jet mixing reactor for desulfurization of molten iron[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(6): 1117-1127. |
| [3] |
Zhuang Liu, Wen-tao Lou, Miao-yong Zhu. Powder transport behavior in RH degasser with powder injection through up snorkel: a transient numerical model[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(6): 1156-1170. |
| [4] |
Qing-hua Xie, Pei-yuan Ni, Toshihiro Tanaka, Mikael Ersson, Ying Li. Flow field, heat transfer and inclusion behavior in a round bloom mold under effect of a swirling flow submerged entry nozzle[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(6): 1211-1221. |
| [5] |
Wei Wang, Cheng Cheng, Li Wan, Jie Tao, Xun-zhong Guo, Chun-mei Liu. Effect of die structure parameters on deformation behavior of bent tube in free bending process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(03): 487-503. |
| [6] |
Ming Zhong, Lei Jiang, Hang-yu Bai, Somnath Basu, Zhan-jun Wang, Cong Wang. Simulating molten pool features of shipbuilding steel subjected to submerged arc welding[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(03): 569-579. |
|
|
|
|
2023, Vol. 30 