| Combined experimental and simulation study on corrosion behavior of B10 copper–nickel alloy welded joint under local turbulence |
| Da-lei Zhang1, Ran Liu1,2, Ying-shuang Liu1,2, Shao-hua Xing2, Zong-hao He1, Yao Qian1, Jin-zeng Liu1, Xiao-hui Dou1, Xin-wei Zhang1 |
| 1 School of Materials Science and Engineering, China University of Petroleum (East China), Qingdao 266580, Shandong, China; 2 State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute, Qingdao 266237, Shandong, China |
|
|
|
|
Abstract The corrosion behavior of B10 copper–nickel alloy welded joints in seawater pipeline system was analyzed under local turbulence induced by weld residual height. The corrosion behavior was evaluated by array electrode technology, morphology and elemental characterization, and COMSOL Multiphysics simulation. The results provide a theoretical basis for the corrosion and leakage of B10 alloy in seawater pipeline under the action of turbulence. The results show that residual height-induced turbulence exhibits a significant effect on the corrosion behavior in different areas of welded joints in B10 alloy. Turbulence can damage some surfaces, causing polarity deflection followed by acceleration of corrosion, or it is easier to form a protective film to slow down corrosion. COMSOL Multiphysics results show that the shear rate and turbulent kinetic energy increase linearly with the increase in residual height and velocity. The corrosion behavior of alloy surface is influenced by controlling the mass transfer rate and surface state.
|
|
|
|
|
|
| Cite this article: |
|
Da-lei Zhang1,Ran Liu,Ying-shuang Liu, et al. Combined experimental and simulation study on corrosion behavior of B10 copper–nickel alloy welded joint under local turbulence[J]. Journal of Iron and Steel Research International, 2023, 30(8): 1598-1612.
|
|
|
|
| [1] |
Yan-xin Qiao, Zhi-bin Zheng, Hao-kun Yang, Jun Long, Pei-xian Han. Recent progress in microstructural evolution, mechanical and corrosion properties of medium-Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(8): 1463-1476. |
| [2] |
Yang Yang, Hui Su, Lan-lan Liu, Song Xu, Zhen Zhong, Xiao-bao Zhou, Tang-qing Wu. Inhibition roles of molybdate and borate on Q235 steel corrosion in resistance reducing agent[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(8): 1477-1489. |
| [3] |
Chen Dong, Shen Qu, Chang-ming Fu, Zhe-feng Zhang. Failure analysis of crevice corrosion on 304 stainless steel tube heat exchanger[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(8): 1490-1498. |
| [4] |
Hai-liang Zhang, Ling-xu Yang, Qian Wang, Jiang-tao Wu, Suo-de Zhang, Chao-liu Zeng. Hot corrosion behaviors of 921A alloy and HVAF-sprayed Fe-based amorphous coating covered with KCl–ZnCl2 salts[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(8): 1537-1549. |
| [5] |
Yong-kuan Zhou, Jia-jie Kang, Guo Jin, Xiu-fang Cui, Jie Zhang, Guo-zheng Ma, Zhi-qiang Fu, Li-na Zhu, Ding-shun She, Yu-yun Yang. Effect of vacuum heat treatment on microstructure and corrosion behavior of HVOF sprayed AlCoCrFeNiCu high entropy alloy coatings[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(8): 1550-1561. |
| [6] |
Wen-jiao Zhang, Yan-li Wang. Performance of TiC coating prepared by in situ conversion of organic carbon film on 316L bipolar plate[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(8): 1562-1573. |
|
|
|
|
2023, Vol. 30 