| Optimization of preparation process of high-strength pellets from Panzhihua ilmenite concentrate |
| Gang-wei Zhou1, Wei Lv1, Fu-rong Chen1, Zheng-gen Liu1, Man-sheng Chu1,2, Xue-wei Lv2 |
| 1 School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China 2 College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China |
|
|
|
|
Abstract The preparation of high-strength pellets from Panzhihua ilmenite concentrate is important for the hydrogen-rich smelting of titania slag and was investigated. The effects of the magnetite concentrate and heating procedure including the preheating temperature and period as well as roasting temperature and period on the compressive strength of the roasted pellets were investigated. High-strength ilmenite concentrate pellets ([2000 N) were prepared by optimizing the roasting process. The addition of magnetite concentrate is beneficial for increasing the compressive strength of the Panzhihua ilmenite concentrate pellet by oxidizing hematite which filled the pseudobrookite particles, functioned as a bridge bond, and improved the interconnection between the grains. The compressive strength can reach up to 2900 N when the ilmenite concentrate pellet with 15% magnetite concentrate is pre-heated above 800 C for 20 min and then roasted at 1250 C for 20 min. In addition, there is an overall upward trend in the compressive strength with an increase in the pre-heating temperature and period as well as the roasting temperature and period. The micromorphology and strengthening consolidation mechanism of Panzhihua ilmenite concentrate pellets were also discussed.
|
|
|
|
|
|
| Cite this article: |
|
Gang-wei Zhou,Wei Lv,Fu-rong Chen, et al. Optimization of preparation process of high-strength pellets from Panzhihua ilmenite concentrate[J]. Journal of Iron and Steel Research International, 2023, 30(12): 2391-2402.
|
|
|
|
| [1] |
Zi-han Wang, Jing Guo, Han-jie Guo1 Bin Li. Thermodynamic and experimental study of high-temperature roasting of blast furnace gas ash for recovery of metallic zinc and iron[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2024, 31(1): 108-120. |
| [2] |
Tao Yang, Jing-shu An, Xing-wang Li, Shuang Liu, Xu Gao, Lei Ma, Jie Lei, Hong-ming Long. Effect of quaternary basicity on reduction behavior of iron-bearing dust pellets[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(7): 1356-1366. |
| [3] |
Ting Wu, Yu-qi Kong, Jiu-chang Zhang, Xin-yu Wang, Lei Ma, Tao Yang, Jie Lei, Hong-ming Long. Agglomeration and bonding mechanism of typical metallurgical solid wastes[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(7): 1390-1400. |
| [4] |
Jun-yi Xiang, Ming-shuai Luo, Xi Lu, Lu-wei Bai, Zhong-peng Zhu, Qing-yun Huang, Sheng-qin Zhang, Kun-peng Guo, Xue-wei Lv. Recovery of vanadium from vanadium slag by composite additive roasting–acid leaching process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(7): 1426-1439. |
| [5] |
Jie Lei, Xu Gao, Jing-shu An, Guang-da Bao, Yu-qi Kong, Hong-ming Long. Drop strength measurement of green pellet based on drop-rebound mechanism[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(11): 2143-2152. |
| [6] |
Yong-li Jin, Jin-tao Jiang, Hong-xing Dai, Xu-dong Zhang, Zeng-wu Zhao. Reaction characteristics of carbon-bearing pellets of Bayan Obo lean iron ores in a static magnetic field[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(09): 1687-1700. |
|
|
|
|
2023, Vol. 30 