| Effect of Quenching Condition on Mechanical Properties, Microstructure and Precipitation Behavior of AISI H13 Steel |
| An-gang Ning1, Yang Liu2, Rui Gao2, Stephen Yue2, Ming-bo Wang3, Han-jie Guo4 |
1 College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, Shanxi, China
2 Department of Mining and Materials Engineering, McGill University, Montreal, QC H3A 0C5, Canada
3 ASSAB Tooling Technology (Chongqing) Co., Ltd., Chongqing 401120, China
4 School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract The effects of austenitizing temperature (1223, 1303, and 1373 K) and holding time (1–1500 s) on the microstructure, mechanical properties, and precipitation behavior of the H13 hot work die steel were investigated. The results indicate a softening phenomenon when H13 steel is austenitized at 1303 K beyond 900 s and 1373 K beyond 600 s, respectively. For the sample held for 1200 s, the tensile strength is found capable of reaching up to 2.2 GPa when quenched from a temperature above 1303 K. Meanwhile, prior-austenite grain size increases with the increase in austenitizing temperature. The kinetic behavior of the precipitates (mainly MC-type carbides) in H13 steel could be elaborated through the principles set forth by the Arrhenius and Avrami equations. Finally, the comprehensive strengthening of the H13 steel was discussed in detail. The results show that the activation energy of the transformed fraction of carbides is higher than that of the diffusion process for common alloying elements (Cr, V, Mo, and Ni) found in the austenite. This suggests that it would be difficult for precipitates to dissolve into the matrix when H13 steel is austenitized at high temperatures. With the increasing austenitizing temperature, the precipitation fraction decreases, and the dislocation density increases. The dislocation strengthening is regarded as the dominant strengthening contributed to yield strength in as-quenched H13 steel.
|
|
Received: 04 January 2022
Published: 25 January 2024
|
|
|
|
| Cite this article: |
|
An-gang Ning,Yang Liu,Rui Gao, et al. Effect of Quenching Condition on Mechanical Properties, Microstructure and Precipitation Behavior of AISI H13 Steel[J]. Journal of Iron and Steel Research International, 2024, 31(1): 143-156.
|
|
|
|
| [1] |
Yan-xin Qiao, Zhi-bin Zheng, Hao-kun Yang, Jun Long, Pei-xian Han. Recent progress in microstructural evolution, mechanical and corrosion properties of medium-Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(8): 1463-1476. |
| [2] |
Jing-xiong Zhong, Li-ying Cao, Mei Li, Shu-ping Wang, Fang Liu, Xue-wei Lv, Xiao-qin Peng. Mechanical properties and durability of alkali-activated steel slag–blastfurnace slag cement[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(7): 1342-1355. |
| [3] |
Hao Liu, Yu-xuan Zhu, Zhou-fu Wang, Yan Ma, Xi-tang Wang. Enhanced slag resistance and mechanical properties of magnesia castables with strontium carbonate addition[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(10): 2021-2030. |
| [4] |
Fei-fei Li, An-rui He, Yong Song, Xiao-qing Xu, Shi-wei Zhang, Yi Qiang, Chao Liu. MDA-JITL model for on-line mechanical property prediction[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(03): 504-515. |
| [5] |
Xue-kui Lian, Yong Li, Yi Xiong, Yong-li Wu, Shun Han, Tian-tian He, Chun-xu Wang, Feng-zhang Ren. Effect of annealing time on microstructure and mechanical properties of cryorolled AISI 310S stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(03): 548-556. |
| [6] |
Rong Zhu, Mai Wang, Zhen-li Mi, Qi Zhang, Xiao-yu Yang, Yong-gang Yang, Yan-xin Wu. Effects of nano-ceramic additives on high-temperature mechanical properties and corrosion behavior of 310S austenitic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(03): 591-600. |
|
|
|
|
2024, Vol. 31 