FEM Simulation for Temperature and Thermal Stress Field of Chamfering-Mold |
WANG Wei-hua,WANG Wen-jun,LIU Yang,CHEN Xia |
Shougang Research Institute of Technology, Beijing 100043, China |
|
|
Abstract Development and application for chamfering-mold has been carried out in order to control the corner transverse crack defect of continuous casting slab effectively and steadily and the satisfactory effect has been acquired. By means of ANSYS FEM software, taking 250mm×2000mm continuous casting slab as object, the temperature field of chamfering-mould of different dimensions, thermal stress field of right-angle-mold and 35mm×35mm chamfering-mold have been calculated. The calculation results show that the lowest temperature of chamfered part reached 918℃ when the chamfer dimension is 35mm×35mm, the minimum temperature of the corner from high temperature tensile curve of the high temperature side is gradually separated from the brittle zone; comparing with rectangular-slab, the chamfering-slab corner stress concentration is completely eliminated. So if the chamfering-mold used the maximum z stress of slab is reduced by 19.2%, transverse corner crack occurrence possibility will be greatly reduced.
|
Received: 24 July 2012
Published: 22 February 2013
|
|
|
|
|
[1] |
GUO Shuai, ZHU Hang-yu, ZHOU Jie, DONG Shuai, LIANG Yin. Effects of inclusions on stress field in low-density steel under compressive loading[J]. Iron and Steel, 2022, 57(7): 63-72. |
[2] |
JIN Hao-yue, SUN Jie, WEI Zhen, WANG Long-jun, HOU Fan, ZHANG Dian-hua. Flatness control analysis of tension levelling process based on finite element method[J]. Iron and Steel, 2022, 57(6): 100-109. |
[3] |
WU Hai-long, CEN Chuan-fu, CAO Yu, ZHONG Shan. Application of ANSYS software in continuous casting[J]. CONTINUOUS CASTING, 2022, 41(1): 1-8. |
[4] |
The-thanh Luyen, Quoc-tuan Pham, Thi-bich Mac, Tien-long Banh, Duc-toan Nguyen. Graphical method based on modified maximum force criterion to indicate forming limit curves of 22MnB5 boron steel sheets at elevated temperatures[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(8): 1009-1018. |
[5] |
LIU Bin, WANG Ming-lin, ZHANG Hui, WU Xuan, YU Yue, WANG Xue-bing. Effect of casting speed on molten steel flow in slab chamfered mould[J]. CONTINUOUS CASTING, 2021, 40(6): 29-37. |
[6] |
DU Feng-ming, LI Da-wei, SA Xiao-xia, HUANG Ruo-xuan, SHEN Yan, HAN Xiao-guang. Non-uniform friction behavior of slab during continuous casting mold[J]. CONTINUOUS CASTING, 2021, 40(4): 21-25. |
|
|
|
|