Oscillation mark in continuous casting slab of 430 ferritic stainless steel |
YE Hong-gang,CHEN Xing-run,MO Zhi-bin,PAN Ji-xiang |
Hongxing Iron and steel Co., Ltd., Jiuquan Iron and Steel Group Corporation, Jiayuguan735100,Gansu, China |
|
|
Abstract Oscillation mark depth and morphology of 430 ferritic stainless steel slabs were observed by optical microscopy. The results show that the metallographic method can achieve high accuracy to measure the oscillation mark depth. The oscillation marks in the edge of 430 slabs are deep and disorder, while the oscillation marks of central is more evenly distributed and shallow. On the upper surface, the average depth of edge oscillation marks and central oscillation marks is 320.847 6 μm and 247.886 μm. On the lower surface, the average depth of edge oscillation marks and central oscillation marks is 301.753 μm and 221.753 6 μm.The micro cracks and segregation are existed at the bottom of the oscillation marks. The oscillation mark depth of 430 slabs is reduced by optimizing the processing parameters of vibration frequency, vibration amplitude, flux viscosity, etc.
|
Received: 16 June 2014
Published: 13 April 2015
|
|
|
|
[1] |
BAI Xiao-lu, ZHANG Xiao-wei, LI Meng-fei, ZHANG Li-qiang. Corner crack controlling of niobium microalloyed steel billet for construction[J]. CONTINUOUS CASTING, 2022, 41(2): 61-65. |
[2] |
MA Fei-yue. Development and prosperity of macrostructure etching process of continuous casting billet[J]. CONTINUOUS CASTING, 2022, 41(1): 9-13. |
[3] |
JIANG Dong-bin, ZHANG Li-feng, CHEN Tian-ming, LI Hong-guang, LI Jian-quan. Characterization of macrosegregation and semi-macrosegregation in continuous casting bloom[J]. CONTINUOUS CASTING, 2021, 40(4): 31-37. |
[4] |
CHANG Zhuo1, 2, YANG Jun1, XU Lijun2, QIU Shengtao2, SHI Pengzhao2,TIAN Yushi2. Study on surface microcracks of Q355R continuous casting slab[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(12): 1296-1306. |
[5] |
ZHANG Yue-xin, ZHANG Li-feng, WANG Ju-jin, NIU Kai-jun, WANG Ya-dong. Prediction of composition distribution of non-metallic inclusions in a billet[J]. Iron and Steel, 2021, 56(10): 74-82. |
[6] |
WU Min, LI Guo-ping, ZOU Yong, WANG Li-xin, WEI Ying-hui. Effect of annealing temperature on microstructure and properties of ferritic stainless steel 441[J]. Iron and Steel, 2021, 56(1): 97-103. |
|
|
|
|