Causes analysis on the thermoplastic brittle region �� of medium manganese steel |
WANG Yu-tian1��WANG Cun-yu1,2��SHI Fa-cai1��TAO Hong-biao3 |
1. Technology Center of Taiyuan Iron and Steel Group Co.�� Ltd.�� Taiyuan 030003��Shanxi�� China 2. East China Branch of Central Iron and Steel Research Institute�� Beijing 100081�� China 3. National Engineering and Research Center of Continuous Casting Technology��Central Iron and Steel Research Institute�� Beijing 100081�� China |
|
|
Abstract Transverse corner crack is likely to occur on slab of medium manganese steel. The thermoplastic of medium manganese steel was studied using Gleeble thermal-mechanical simulator�� and the causes of the brittle region �� were analyzed through microstructure characterization and thermodynamics analysis. The results show that the brittle region ��was occurred at the temperature of 550-775 �棬 and the ferrite phase transformation induced by deformation cause the lowest thermoplasticity at the deformation temperature of 750 ��.Therefore�� at the practical process�� the quantity of water in the secondary cooling zone of continuous casting should be controlled carefully to avoid the corner crack of continuous cast billet.
|
Received: 14 September 2015
Published: 13 January 2016
|
|
|
|
[1] |
LIU Wei��ZHENG Meng-yao��WANG Zhi-lei��LIU Jin��ZHENG Shao-chuan�� GAO Xiu-hua. Influence of alloy element and microstructure on corrosion behavior of medium-Mn steel in a simulated marine splash zone[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 75-80. |
[2] |
LIU Chun-quan,,PENG Qi-chun,,DENG Ming-ming��XU Jing-bo,LI Wei,PENG Sheng-tang. Research situation of Mn-Al medium manganese steel for 3rd generation automobile sheet[J]. Chinese Journal of Iron and Steel, 2017, 29(6): 431-440. |
[3] |
QIU Chun-gen,,XU Li-jun,SHI Peng-zhao,,QIU Sheng-tao,ZHAO Hong-jin. Formation mechanism of brittle zone III of microalloyed steel[J]. Chinese Journal of Iron and Steel, 2017, 29(2): 161-166. |
[4] |
LU Jue-yu��DU Cheng-wei��LI Yang��ZHANG Jia-quan��JIANG Zhong-kuai��SU Rui-xian��WANG Hong-feng��ZHOU Xiu-li. Effect of holding time on austenite grain size of J55 casting slab[J]. Chinese Journal of Iron and Steel, 2016, 41(5): 67-71. |
[5] |
LIU Gui-jiang��BAO Wen-quan��HAN Feng-jun��AN Jie��WANG Zhe. Analysis on the surface defects of hot rolled bar[J]. Chinese Journal of Iron and Steel, 2016, 41(4): 64-68. |
[6] |
WANG Chang��XU Hai��feng��HUANG Chong��xiang��CAO Wen��quan��DONG Han. Evolution of ART��annealed microstructure and partition behavior of manganese in medium manganese steel[J]. Chinese Journal of Iron and Steel, 2016, 28(4): 38-46. |
|
|
|
|