| Effect of holding time on austenite grain size of J55 casting slab |
| LU Jue-yu1，DU Cheng-wei1，LI Yang1，ZHANG Jia-quan1，JIANG Zhong-kuai2，SU Rui-xian2，WANG Hong-feng2，ZHOU Xiu-li2 |
| （1. School of Metallurgical and Ecological Engineering， University of Science and Technology Beijing， 100083， China：2. Shanghai Meishan Steel， Nanjing， 210039， China |
|
|
|
|
Abstract The size of austenite grain plays an important role on the hot ductility of continuous casting slab， and the abnormal large austenite grain also relate to the defects on the strand surface. The results of experimental research on the effect of holding time at 1 350 ℃ on austenite grain size of J55 are compared with related literatures. It shows that the austenite grain size of J55 gets coarser with the increase of holding time at 1 350 ℃.With reference to previous researches， to get a similar level of austenite grain size in the process of continuous casting， the sample of J55 should be held for at least 30 minutes at 1 350 ℃.The results also suggest that the way usually used for high temperature thermal tensile test simulation to test the hot ductility of specimens is probably not considering the size of austenite grains during continuous casting， the results of which may not represent the hot ductility of high temperature slab.
|
|
Received: 26 May 2016
Published: 17 November 2016
|
|
|
|
| [1] |
Ji-yuan Luo, Xin-ming Ren, Xiao-chuan Chong, Dong-hai Ding, Bei-yue Ma, Guo-qing Xiao, Jing-kun Yu. Recent progress in synthesis of composite powders and their applications in low-carbon refractories[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1041-1051. |
| [2] |
Chao Yu, Bo Dong, Yu-feng Chen, Bei-yue Ma, Jun Ding, Cheng-ji Deng, Hong-xi Zhu, Jing-hui Di. Enhanced oxidation resistance of low-carbon MgO–C refractories with ternary carbides: a review[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1052-1062. |
| [3] |
Qian Sun, En-hui Wang, Xin-mei Hou, Zhi-jun He, Tong-xiang Liang. Effect and mechanism of nano-Ca10(PO4)6(OH)2 additive on compressive strength of calcium aluminate cement at high temperature[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1063-1072. |
| [4] |
Rui-qiang Bai, Si-yang Liu, Fei-xiong Mao, Yuan-yuan Zhang, Xin Yang, Zhi-jun He. Wetting and corrosion behavior between magnesia–carbon refractory and converter slags with different MgO contents[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1073-1079. |
| [5] |
Bei-yue Ma, Xin-ming Ren, Zhi Gao, Fan Qian, Zhao-yang Liu, Guo-qi Liu, Jing-kun Yu, Gao-feng Fu. Influence of pre-synthesized Al2O3–SiC composite powder from clay on properties of low-carbon MgO–C refractories[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1080-1088. |
| [6] |
Mao-qi Ju, Man-fei Cai, Yong-he Liang, Jian-hua Nie, Meng-zhen Guo. Application of calcium alumino-titanate to taphole clay[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1089-1100. |
|
|
|
|
2016, Vol. 35 