Analysis and Improvement of cracking causes of swrch22a round head cross bolt |
YANG Qi-min,NONG Zhi-jiang,FENG Bao,AO Yong-ming,XIE Jie-zhi,XIE Gui-long |
(Baosteel Group Guangdong Shaoguan Iron and Steel Co., Ltd., Shaoguan 512123, Guangdong China) |
|
|
Abstract When the cold heading steel rod SWRCH22A is deformed during use, the head of the bolt undergoes cold heading and cracking during the processing of the round head cross bolt. In order to improve the performance of SWRCH22A wire rod and reduce the cracking probability of cold heading, the metal cracking specimens were detected and analyzed by means of metallographic examination, scanning electron microscopy and energy spectrum analysis. The results show that there is no obvious surface defect in the position corresponding to the stem at the cracked head of the bolt, and there is a long slag inclusion on the near surface. The composition of the slag is similar to that of the continuous casting mold. The main reason for the cracking of the SWRCH22A round head cross bolt is that the slag in the continuous casting process causes the slag on the near surface of the material to crack during cold forming.
|
Received: 21 April 2018
Published: 29 June 2018
|
|
|
|
[1] |
刘远.冷镦钢开裂原因分析及质量改进措施[J].金属材料与冶金工程,2008,36(6):33-36.
|
[2] |
刘春林,农之江,张志明.冷镦钢线材冷顶锻开裂问题分析及改善措施[J].南方金属,2015,6:30-33.
|
[1] |
ZHOU Qiu-yue, ZHU Tan-hua, ZHANG Li-feng, CHEN Wei, YUAN Tian-xiang, LIU Zhen-tong. Large eddy simulation on quantitative influence of unsteady casting on mold slag entrainment[J]. Iron and Steel, 2022, 57(4): 68-78. |
[2] |
WU Xu-feng, ZHANG Cai-gui, WANG De-yong. Effect slag modification on vortex entrapment in ladle[J]. CONTINUOUS CASTING, 2022, 41(2): 41-46. |
[3] |
LI Xiang-long, FENG Sheng-qiang, ZHANG Zhi-xiao, WU Guang-jun, ZHANG Pei, QU Tian-peng. Effect of casting speed on slag entrapment in continuous casting mold[J]. CONTINUOUS CASTING, 2022, 41(2): 100-108. |
[4] |
REN Ying, LI Xin-zhe, YUAN Tian-xiang, CHEN Wei, ZHOU Hai-chen, ZHANG Li-feng. Source analysis and control status of slag defects on surface of hot-rolled coil[J]. Iron and Steel, 2022, 57(1): 13-27. |
[5] |
WEN Ju-wen, GUO Yin-tao, ZHAO Xiao-hu, QIN Cong, LI Hui-ya. Industrial test and application on high casting speed mold flux for low carbon steel slab[J]. CONTINUOUS CASTING, 2021, 40(2): 61-65. |
[6] |
YUAN Gang, YANG Zhi-chao, TANG Shu-ping, KONG Yong-jiang, YANG Yun-chao, LIU Gui-fu. Analysis and control of inclusion defects of tinplate steel slab[J]. CONTINUOUS CASTING, 2020, 39(6): 62-67. |
|
|
|
|