Study on the typical quality defect control process of 65Mn billet |
LIN Peng,ZHANG Hong-cai,MA Jian-chao,ZHAI Wan-li,YIN Chuan-lei |
(Jiangsu Shagang Group Huaigang Special Steel Stock Co., Ltd., Huaian 223002, Jiangsu, China) |
|
|
Abstract There is off-square,angle concaves and corner cracks in 200 mm square billet of 65Mn in a certain steel plant,which are caused by the uneven cooling of mold and secondary cooling zone by analyzing. The process optimization schemes of enlarging the[R]Angle and the taper and increasing the secondary cooling water flow have been carried out. The method of enlarging the[R]Angle and the taper of the mold improve the heat transfer of the mold cooling. The increase of the secondary cooling water and the water pressure of the foot roller improve the cooling effect of the secondary cooling section. The cooling uniformity of casting billet has been increased. The test shows the quality problems of off-square,angle concaves and corner cracks have been controlled effectively and the quality of casting billet has been greatly improved.
|
Received: 01 March 2018
Published: 29 September 2018
|
|
|
|
[1] |
Cai kaike,Sun Yanhui,Han chuanji.The “Zero Defect” Philosophy of Controlling Strand Quality for Steel Continuous Casting[J]. Continuous casting.2011(addition): 288~298.
|
[2] |
朱苗勇,杜刚,阎立懿等.现代冶金学(钢铁冶金卷)[M].北京:冶金工业出版社,2010:344-346.
|
[3] |
蔡开科.连铸坯质量控制[M].北京:冶金工业出版社,2010:216-217.
|
[4] |
王志道,万体娅等.低倍检验在连铸生产中的应用和图谱[M].北京:冶金工业出版社,2009:15-16.
|
[5] |
常桂华,曹亚丹,吕志升等.连铸坯的高温力学性能分析[J].鞍钢技术,2007(6):25-29.
|
[1] |
ZHENG Yuan-shou. High speed production technology of 160 mm× 160 mm continuous casting in Sangang[J]. CONTINUOUS CASTING, 2020, 39(3): 10-13. |
[2] |
LI Fu-shuai,BAI Ju-bing,NI Sai-zhen,QIAN Liang,XIE Chang-chuan,WANG Fang-fang. Thermal Response of Copper Mold and Dynamic Response of the Mold Oscillation in the Continuous Casting of Billet[J]. Chinese Journal of Iron and Steel, 2014, 33(2): 26-31. |
[3] |
HE Tian-ke. Causes and Countermeasures of Triangle Area Crack in Slab[J]. Chinese Journal of Iron and Steel, 2012, 31(4): 43-46. |
[4] |
TONG Xin;SONG Mantang. Formation Mechanism and Prevention of Center and TriangleZone Cracks in Continuous Cast Slabs[J]. Chinese Journal of Iron and Steel, 2009, 28(1): 36-0. |
|
|
|
|