热轧板卷LF轻处理技术的研究与应用

doi:10. 13228/j. boyuan. issn1005-4006.20180065

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract Lianyuan steel developed light LF refining technology for high-grade hot rolled coil relying on KR one-button desulfurization， accurately pre-deoxidation after BOF and automatic bottom-blowing at argon station. The stopper rod rising problem was resolved by adding aluminum one time at LF， controlling [O] content in liquid steel before adding aluminum between 40×10－6 and 100×10－6， soft blowing sustaining 8 mins after adding aluminum. The T.Fe content in top slag in ladle at LF beginning could be controlled below 3% by top slag modified and accurately pre-deoxidation during tapping. This work ensures that the steel purity did not getting worse through light LF refining process. The sulfur content of liquid steel in tundish through light LF refining was less than that through traditional LF refining process. The sulfur content was 0.003 5% and 0.004 6%. Through this technology， not only the cost was reduced significantly but also the oxygen and nitrogen content was 10×10－6 lower， inclusion was less and fatigue property was better than those of traditional process.

Key words： Light LF refining Inclusion Low cost Fatigue Property Hot rolled coil

Received: 17 July 2018 Published: 06 November 2018

PACS:

TF769.2

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	XU Gang-Jun
	LIU Bang
	DUO Ya-Fei

Cite this article:

XU Gang-Jun,LIU Bang,DUO Ya-Fei. Research and application of light LF refining technology on hot rolled coil[J]. , 2018, 37(5): 19-25.

URL:

http://www.chinamet.cn/Jweb_lz/EN/10. 13228/j. boyuan. issn1005-4006.20180065 OR http://www.chinamet.cn/Jweb_lz/EN/Y2018/V37/I5/19

[1]	彭其春,邹健,邱雷等.KR-BOF-LF-CC生产汽车大梁钢LG510L洁净度的研究[J].武汉科技大学学报（自然科学版）,2014,(2):111-115.
[2]	吴菊环.汽车结构用SAPH440热轧钢板的试制[J].轧钢,2011,28(1):63-67
[3]	郭子峰,冯军,白永立等.首钢汽车结构用热轧酸洗带钢SAPH440的开发[J].锻压技术,2015,40(2):60-64.
[4]	向华,健龙,新琰.铁水预脱硫在安钢的应用效果分析[J].河南冶金,2017,25(4):24-26.
[5]	夏金魁,曹龙琼,张青山.转炉炼钢流程硫含量控制[J].武钢技术,2011,49(4):12-14.
[6]	吕志勇,牛兴明,张宏亮.炼钢流程硫含量经济性控制实践[J].鞍钢技术,2016,401(5):48-52.
[7]	周业连,何奇,邓志银等. 210t BOF-RH-CC流程钢包顶渣改质处理对超低碳钢夹杂物的影响[J].金属材料与冶金工程,2015,36(3):38-42.
[8]	刘彭,罗钢,丁胜强等.超低碳钢顶渣改质工艺优化[J]. 金属材料与冶金工程,2015,43(3):27-30.
[9]	舒宏富,刘浏,刘学华.钢包顶渣改质对ＩＦ钢夹杂物的影响[J].炼钢,2016,32(3):55-59.
[10]	姜玉龙,郑万,齐盼盼等.150t LF精炼喂钙线处理钢中夹杂物的演变[J].特殊钢,2016,37(3):8-12.
[11]	赵烁.重钢AFT702和 CDQ203 钢种经济洁净化工艺基础及应用研究[D].重庆大学,2014.
[12]	隋亚飞,罗钢,王慎德等. 钙处理对涟钢高强机械用钢夹杂物的影响[J].钢铁研究,2017,45(4):13-18.
[13]	蔡开科，连铸坯质量控制[M].北京，冶金工业出版社，2010.
[14]	洁净钢—洁净钢生产工艺技术[M]. 北京，冶金工业出版社，2009.
[15]	郭上型,王建军,周俐等.BOF-LF-VD-CC工艺生产车轮钢的N含量控制[J].钢铁钒钛,2007,28(4):52-55,70.
[16]	氧工艺对钢中夹杂物的影响[J].钢铁研究学报，2016,28（6）25-30.
[17]	新华，钢铁冶金–炼钢学 [M]，高等教育出版社，2007.
[18]	稀钴，钢铁冶金原理[M]，冶金工业出版社，2006.
[19]	Liu C,Bhole S D. Challenges and developments in pipeline weldability and mechanical properties[J]. Science and Tech- nology of Welding and Joining, 2013，18(2):169.
[20]	Beidokhti B, Dolati A, Koukabi A H. Effects of alloying ele- menu and microstructure on the susceptibility of the welded HSLA steel to hydrogen-induced cracking and sulfide stress cracking[J]. Materials Science and Engineering, 2009，507 A(1/2):167.