| Feasibility research on the increasing of casting speed for gear steel billet treated by PMO technology |
| HE Xi1，LIU Yu1，TENG Li-Hong1，ZHU Fu-Qiang1，LIU Hai-Ning2，CAO Tian-Yi2，LI Ren-Xing2 |
（1. Zenith Steel Group Company Limited， Changzhou 213011， Jiangsu， China
2. Center for Advanced Solidification Technology，Shanghai University， Shanghai 200444， China） |
|
|
|
|
Abstract The feasibility of increasing of casting speed for 20CrMnTi gear steel billet treated by PMO technology was investigated. The experimental results show that when the casting speed is increased from 0.94 m/min to 0.99 m/min， the area rate of equiaxed grain， the degree of porosity and macro-segregation index in the centerline are correspondingly changed from 15.6%， 0， 1.21 to 13.3%， 0.5， 1.36， respectively. By contrast， for the billet treated by PMO， the area rate of equiaxed grain is only decreased from 26.0% to 23.0%， and the degree of porosity and macro-segregation index in the centerline keep 0 and 1.1， respectively. It indicates that it is feasible to increase the casting speed for the billet treated by PMO because the billet quality still can be guaranteed.
|
|
Received: 11 October 2018
Published: 29 January 2019
|
|
|
|
| [1] |
Fan Qian, Hua-long Li, Wen-gang Yang, Hai-rong Guo, Guo-qi Liu, Hong-xia Li, Bei-yue Ma. Corrosion resistance of BN–ZrO2 ceramics with different additives by molten steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1101-1109. |
| [2] |
ZHANG Xiang，XIE Qinghua，NI Peiyuan，LI Ying. Flow behavior of molten steel in SEN during fullnozzle selfswirling flow continuous casting[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 629-638. |
| [3] |
ZHAO Xianjiu1,2，ZHANG Jieyu2,3，LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
| [4] |
SHANG Ting-rui, WANG Wei-ling, KANG Ji-bai, ZHU Miao-yong, LUO Sen. In situ observation of solidification under transient and average cooling rate of 20CrMnTi continuous casting[J]. Iron and Steel, 2022, 57(7): 73-85. |
| [5] |
CHEN Bin, LI Hai-bo, JI Chen-xi, LIU Guo-liang, ZHOU Hai-chen. Influence of casting parameters on level fluctuations and its industrial application[J]. Iron and Steel, 2022, 57(7): 86-94. |
| [6] |
KANG Yong-lin, ZHU Guo-ming, JIANG Min, WANG Guo-lian, LIU Peng-tao, XU Hai-wei, XIE Cui-hong, WEI Yun-fei, SHEN Kai-zhao, LIU Yang. Slab continuous casting by big roll heavy reduction and extra thick plate rolled by low compression ratio[J]. Iron and Steel, 2022, 57(7): 95-105. |
|
|
|
|
2018, Vol. 37 