Conditions of viscosity measurement of mold fluxes for continuous casting |
BIN Xi |
Pangang Group Panzhihua Vanadium Steel Co., Ltd., Manufacturing Department, Panzhihua 617000, Sichuan, China |
|
|
Abstract Improving the ratio of continuous casting is an effective measure to improve the production efficiency and rolling yield, save energy and reduce cost, and is also a key index to reflect the smelting level of steel mills. The viscosity standard of continuous casting protective slag recommended by China's metallurgical industry——internal cylinder rotation method is not clear because of its the guidance of the test method, which leads to large fluctuation of the measurement results in practical work. Combined with the actual work,the test conditions of the viscosity of continuous casting protective slag were studied. The results show that when the carbon content of the sample is less than 0.5%, the length of the constant temperature zone of the furnace body meets the requirements, the temperature fluctuation of the constant temperature zone is less than 3 ℃, the graphite head immersed in the melt was controlled at 10-20 mm, the furnace body was sealed, and the excellent graphite dry pot is used, the furnace body is sealed. The determination result is stable and reliable.
|
Received: 10 January 2020
|
|
|
|
[1] |
钟云涛,李强.保护渣在连铸机中的应用[J].连铸,2013,38(4):9.
|
[2] |
臧雪松,徐安军,李稷,等.炼钢-连铸区段天车调度的多目标建模与求解[J].中国冶金,2020,30(2):68.
|
[3] |
邓小旋,潘宏伟,季晨曦,等.常规低碳钢板坯的高速连铸工艺技术[J].钢铁,2019,54(8):70.
|
[4] |
王芳,李娇,金桂香,等.超低碳钢连铸保护渣发展专利现状分析[J].连铸,2015,40(2):1.
|
[5] |
朱先飞,文光华,蒲大志,等.稳态导热下连铸保护渣固态渣膜有效导热系数的研究[J].连铸,2018,43(3):25.
|
[6] |
余杰,王万林,肖丹,等.MgO和BaO对CaO-Al2O3系保护渣熔化与结晶行为的影响[J].连铸,2018,43(4):37.
|
[7] |
宋土顺,朱立光,王杏娟,等.Q345B钢保护渣显微结构及矿相组成研究[J].连铸,2017,42(5):29.
|
[8] |
汪金良,王龙君.覆铜板废边角料熔炼渣黏度研究[J].有色金属:冶炼部分,2020(3):23.
|
[9] |
雷志亮,张东栋,梅峰,等.超低碳保护渣控制钢水增碳的研究[J].连铸,2018,43(5):49.
|
[10] |
王谦,何生平,李玉刚,等.中国连铸保护渣技术现状及发展需求[J].连铸,2014,39(5):1.
|
[11] |
巩飞,董大西,陈良勇,等.合金钢大方坯连铸坯表面质量控制技术[J].连铸,2013,38(2):42.
|
[12] |
曹洪文,孔繁芬.炉渣粘度测量装置[J].化工冶金,1979(1):43.
|
[13] |
龙潇,何生平,王谦.高碱度连铸结晶器保护渣液渣膜粘度特性研究[J].连铸,2011,36(增刊1):49.
|
[14] |
李运平. 结晶器保护渣黏度检测实践[J].理化检验:物理分册,2018,54(9):669.
|
[15] |
王常珍. 冶金金物理化学研究方法[M]. 3版.北京:冶金工业出版社,2002:310.
|
[16] |
艾新港,韩东,李胜利,等.外加液态保护渣连铸生产实践与前景展望[J].钢铁,2019,54(8):132.
|
[17] |
刘克,曾义君,韩毅华,等.电磁场对连铸保护渣流变特性的影响[J].中国冶金,2020,30(4):31.
|
[1] |
ZHAO Xianjiu1,2,ZHANG Jieyu2,3,LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
[2] |
WANG Xu-feng, WANG Qiang-qiang, ZHANG Xu-bin, WANG Qian, HE Sheng-ping. Effect of AlN on properties of CaO-SiO2 based mold fluxes for high-Al steel[J]. Iron and Steel, 2022, 57(5): 64-71. |
[3] |
YAN Xiao-peng, LIU Lei, HAN Xiu-li, WANG Yin-hui, ZHANG Di. Effect of boron on microstructure of fluorine-free mold fluxes[J]. Iron and Steel, 2022, 57(5): 72-80. |
[4] |
JIANG Xianggui1, REN Ying1, YANG Wen1, ZHANG Lifeng2. Research progress on deformation of inclusions in steel during rolling[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(4): 297-308. |
[5] |
LIU Chang-wei, ZOU Zhuo-ming. Application of robot automatic mould fluxes adding technology in Ningbo Iron and Steel Works[J]. CONTINUOUS CASTING, 2022, 41(3): 71-75. |
[6] |
PIAO Zhan-long, WANG Xing-juan, ZHANG Cai-jun, ZHU Li-guang, LI Shao-ying, WANG Bo. Steel-slag interface reaction behavior in continuous casting mold of high titanium steel[J]. Iron and Steel, 2022, 57(3): 61-70. |
|
|
|
|