Influencing factors analysis and production practice of tundish argon filling replacement in continuous casting |
YANG Ke-zhi |
Technology Center, Ma'anshan Iron and Steel Co., Ltd., Ma'anshan 243000, Anhui, China |
|
|
Abstract Aiming at the poor results of argon filling replacement in the tundish before the start of pouring in No.4 Steel-making and Rolling General Plant of Ma'anshan Iron and Steel Co., Ltd., the influencing factors of the tundish argon filling replacement were studied under cold measurement experiments by using a portable flue gas analyzer,and the optimization measures were proposed. The results showed that increasing the pressure of argon filling, having a good seal of the bake holes of the tundish, between the tundish lids and the tundish lids between the tundish can effectively improve the effect of argon filling replacement. Under normal production conditions after optimization, when the diameter of the tundish argon filling tube is ø30 mm and the argon filling pressure is 1.4-1.6 MPa, the oxygen volume fraction after argon filling can be effectively reduced to less than 1%. When the diameter of the tundish argon filling tube is ø15 mm and the argon filling pressure is 0.8-1.0 MPa, the oxygen volume fraction after argon filling can be effectively reduced to less than 2%
|
Received: 15 May 2020
|
|
|
|
[1] |
朱坦华,周秋月,任英,等. 二次氧化过程IF钢中间包中夹杂物演变行为[J]. 钢铁,2020,55(3):35.
|
[2] |
李小傲,郭卓,陈敏,等. SPHD钢中夹杂物在RH-CC工序的演变规律[J]. 材料与冶金学报,2019,18(2):92.
|
[3] |
苑鹏,章军,刘道正,等. 超低碳钢中Al-Ti夹杂物的形成机理和控制技术[J]. 钢铁,2018,53(7):24.
|
[4] |
袁方明,王新华,李宏,等. 不同浇铸阶段IF钢连铸板坯洁净度[J]. 北京科技大学学报,2005,27(4):43.
|
[5] |
杨文,薛勇强,曹晶,等. 低碳铝镇静钢头坯洁净度研究[J]. 钢铁,2011,46(9):34.
|
[6] |
王超. ER70S-G钢水可浇性提升研究[J]. 河北冶金,2019(8):55.
|
[7] |
谷志敏,王文辉,杨立永,等. 洁净钢控制技术的研究与应用[J].河北冶金,2019(9):40.
|
[8] |
曹磊,王玉民,丁中,等. 开浇第一炉连铸坯夹杂物形成原因与控制措施[J]. 中国冶金,2014,24(2):9.
|
[9] |
吴礼旺. 连铸保护浇铸工艺改进[J]. 世界有色金属,2019(2):219.
|
[10] |
武光君. 板坯连铸中间包气幕挡墙技术开发与应用[J]. 连铸,2018 (1):34.
|
[11] |
武光君,王中学,高立福,等. 连铸中间包环形气幕挡墙吹氩冶金技术开发与应用[J].连铸,2019 (5):21.
|
[12] |
赵培林,韩文习,杨志杰,等. 夹杂物对海工用H型钢冲击韧性影响及分析[J]. 中国冶金,2020,30(2):74.
|
[13] |
沈昶,赵沛. 中碳铝镇静钢连铸开浇工艺对夹杂物变化的影响[J].安徽工业大学学报:自然科学版,2015,32(2):105.
|
[14] |
刘中柱,蔡开科. 纯净钢生产技术[J]. 钢铁,2000,35(2):64.
|
[15] |
沈维美. 惰性气体置换时用气量的计算[J]. 油气储运,1996,15(1):21.
|
[1] |
Fan Qian, Hua-long Li, Wen-gang Yang, Hai-rong Guo, Guo-qi Liu, Hong-xia Li, Bei-yue Ma. Corrosion resistance of BN–ZrO2 ceramics with different additives by molten steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1101-1109. |
[2] |
ZHANG Xiang,XIE Qinghua,NI Peiyuan,LI Ying. Flow behavior of molten steel in SEN during fullnozzle selfswirling flow continuous casting[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 629-638. |
[3] |
ZHAO Xianjiu1,2,ZHANG Jieyu2,3,LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
[4] |
SHANG Ting-rui, WANG Wei-ling, KANG Ji-bai, ZHU Miao-yong, LUO Sen. In situ observation of solidification under transient and average cooling rate of 20CrMnTi continuous casting[J]. Iron and Steel, 2022, 57(7): 73-85. |
[5] |
CHEN Bin, LI Hai-bo, JI Chen-xi, LIU Guo-liang, ZHOU Hai-chen. Influence of casting parameters on level fluctuations and its industrial application[J]. Iron and Steel, 2022, 57(7): 86-94. |
[6] |
KANG Yong-lin, ZHU Guo-ming, JIANG Min, WANG Guo-lian, LIU Peng-tao, XU Hai-wei, XIE Cui-hong, WEI Yun-fei, SHEN Kai-zhao, LIU Yang. Slab continuous casting by big roll heavy reduction and extra thick plate rolled by low compression ratio[J]. Iron and Steel, 2022, 57(7): 95-105. |
|
|
|
|