Analysis of surface and internal defects for continuous casting billet of 82A tire cord steel |
CHEN Bo-tao1, WANG Feng-kang2, ZENG Jie2, WANG Wan-lin2, JU Yin-jun1 |
1. Quality Department,Xiangtan Iron and Steel Co.,Ltd., Hunan Valin, Xiangtan 411101, Hunan, China; 2. School of Metallurgy and Environment, Central South University, Changsha 410083, Hunan,China |
|
|
Abstract The surface crack defects and central segregation of cord steel are the key factors affecting the billet quality. The macro defect analysis on the surface of billet, micro morphology characterization of crack, Gleeble high temperature mechanical properties and central segregation measurements are applied, and the surface and internal quality defects of continuous casting 150 mm×150 mm billet of 82A cord steel under steady and unsteady state are analyzed. The results show that the distance between the vibration marks of the billet is 13 mm and the vibration marks at the corners are disordered. Obvious transverse cracks are observed at the vibration mark trough and pit on the surface of unsteady billet, but no transverse cracks are appeared in the steady-state samples. Moreover, an obvious central crack with a length of 55 mm along the central shrinkage cavity in the billet is found and the average central carbon segregation index of the billet is 1.09. Based on the analysis of high temperature mechanical and cracks morphology, the appearance of surface cracks is mainly related to the straightening in the low-temperature brittle zone due to uneven cooling under the unsteady condition, The local temperature is in the third brittle temperature zone during bending and straightening. An obvious liquid film appeared on the surface of the inner central crack, which was formed at the solidification stage of the first brittle zone.
|
Received: 27 September 2021
|
|
|
|
[1] |
黄宝,何立波,高真风,等. 亚洲帘线钢生产现状级发展趋势[J].金属制品,2011 (6): 43.
|
[2] |
Lee S K, Ko D C,Kim B M. Pass schedule of wire drawing process to prevent delamination for high strength steel cord wire[J]. Materials and Design, 2009,30(8):2919.
|
[3] |
牛凯军, 杨文, 张立峰, 等. 帘线钢凝固过程夹杂物生成热力学及工业实践[J]. 钢铁, 2020, 55(6): 61.
|
[4] |
王向红,肖微,张正林,等. 异型中间包结构优化对帘线钢夹 杂物的影响[J]. 中国冶金, 2019, 29(2): 53.
|
[5] |
雷家柳,赵栋楠,朱航宇,等. 高强度帘线钢中氮化钛夹杂的固溶行为分析[J]. 中国冶金, 2018, 28(12): 31.
|
[6] |
易顺,陶勇,阮方,等. 帘线钢凝固过程中钛和氮偏析及TiN夹杂尺寸计算[J]. 钢铁, 2016, 51(4): 70.
|
[7] |
王昆鹏,姜敏,赵昊乾,等. 帘线钢生产过程中氧化物夹杂的演变规律[J]. 钢铁, 2016, 51(4): 31.
|
[8] |
丁瑞锋, 张大伟, 王艳红,等. 帘线钢连铸坯中心偏析控制技术的应用现状[J].上海金属,2017,39(4):75.
|
[9] |
雷家柳,薛正良,朱航宇,等. 子午线轮胎用帘线钢非金属夹杂物的研究进展[J].钢铁研究学报,2018,30(11):847.
|
[10] |
萧忠敏. 武钢炼钢生产技术进步概况[M].北京:冶金工业出版社,2003.
|
[11] |
王勇. 钢帘线表面和性能质量控制工艺的研究[D].武汉:武汉科技大学,2007.
|
[12] |
ZENG J,CHEN W Q,YANG Y D. Effect of permanent magnet stirring on internal quality of steel[J]. Ironmaking and Steelmaking, 2018,45(6):576.
|
[13] |
胡志勇, 陈兴华, 唐萍, 等. 过热度对帘线钢连铸方坯碳偏析的影响[J]. 连铸,2017 (5): 2.
|
[14] |
李茂印,李京社,左小坦,等.合金元素含量对C82DA钢铸坯维管组织的影响[J].连铸,2017 (1):64.
|
[15] |
GUO D W,HOU Z B,PENG Z Q, et al. Influence of superheat on macrosegregation in continuously cast steel billet from statistical maximum viewpoint[J]. ISIJ International, 2021,61(3):844.
|
[16] |
HAN Y S,YAN W,ZHANG J S,et al. Comparison and integration of final electromagnetic stirring and thermal soft reduction on continuous casting billet[J]. Journal of Iron and Steel Research International, 2020,28(2):160.
|
[17] |
李明,胡志勇,陈兴华. 南钢转炉流程生产高品质帘线钢的实践[J].中国冶金,2018,28(4):40.
|
[18] |
曹磊,祭程,杨吉林,等. 轻压下帘线钢大方坯成分偏析特征及形成机制[J].钢铁, 2010,45(8):44.
|
[19] |
蔡开科. 连铸坯质量控制[M]. 北京:冶金工业出版社, 2010.
|
[20] |
曾杰, 陈伟庆, 曹长法, 等. 轻压下对82B钢矩形坯内部质量的影响[J].炼钢,2015,31(4):63.
|
[21] |
ZENG J,CHEN W Q,ZHANG S L,et al. Development and application of final permanent magnet stirring during continuous casting of high carbon rectangular billet[J]. ISIJ International,2015,55(10):2142.
|
[22] |
Won Y M, Han H N, Yeo T J, et al. Analysis of solidification cracking using the specific crack susceptibility[J]. ISIJ International, 2007, 40(2):129.
|
[1] |
ZHOU Qiu-yue, ZHU Tan-hua, ZHANG Li-feng, CHEN Wei, YUAN Tian-xiang, LIU Zhen-tong. Large eddy simulation on quantitative influence of unsteady casting on mold slag entrainment[J]. Iron and Steel, 2022, 57(4): 68-78. |
[2] |
LI Ning1, WANG Lu1, LI Chengzhi2, WANG Peng2, REN Wenqiang2, XUE Zhengliang1,2. Precipitation thermodynamics and formation mechanism of Ti inclusions in hypereutectoid tire cord steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(3): 200-211. |
[3] |
LI Yu-di, JANG Zhong-kuai. Research on cleanliness in unsteady casting slabs of IF steel[J]. CONTINUOUS CASTING, 2022, 41(2): 89-94. |
[4] |
WANG Jiahui1,2,3,FANG Qing1,2,3,ZHU Shuang1,2,3,LI Yang1,2,3,ZHANG Hua1,2,3. Effect of topswirling turbulence inhibitor on flow behaviors of a singlestrand slab casting tundish[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(7): 575-583. |
[5] |
WANG De-yong, QUAN Qi, QU Tian-peng, ZHOU Xing-zhi, LI Xiang-long, CHEN Gang. Physical modeling on unsteady flow behavior of molten steel in single strand tundish[J]. CONTINUOUS CASTING, 2021, 40(5): 60-68. |
[6] |
GUO Liang-liang, WANG Ying-chun, XU Guo-dong. Analysis of surface cracking mechanism of high nitrogen and molybdenum alloy continuous casting[J]. CONTINUOUS CASTING, 2021, 40(4): 26-30. |
|
|
|
|