Three-dimensional distribution on macro inclusions in surface layer of IF steel slabs |
DENG Xiao-xuan1,2, LI Hai-bo1,2, JI Chen-xi1,2, CHEN Bin1,2, ZHU Guo-sen1,2 |
1. Research Institute of Technology, Shougang Group Co., Ltd., Beijing 100043, China; 2. Beijing Key Laboratory of Green Recyclable Process for Iron and Steel Production Technology, Beijing 100043, China |
|
|
Abstract The distributions of macro-inclusions plays an significant role in surface quality of cold rolled steel sheets. The three-dimensional distribution of inclusions over 100 μm in 20 mm surface of IF steel slab was studied by ASPEX automatic detection method and layer-by-layer planing method.It is found that three kinds of macro inclusions were detected, bubbles, alumina plus bubbles and brick alumina and their number percentage occupy 72%、26% and 2%,respectively. The large sized macro inclusions mainly concentrated within the upper roll center zone and stagnant zone below the submerged entry nozzle (SEN) bottom according to the full scale water modeling of mold domain. Eliminating the dead zone in mold is helpful to reduce the large size inclusions and improve the surface quality of rolled products.
|
Received: 31 January 2022
|
|
|
|
[1] |
于会香, 潘明,杨德新.超低碳IF钢脱氧合金化过程中夹杂物的行为[J].钢铁,2020, 55 (6): 46.
|
[2] |
徐国军, 胡华东, 田川,等. Al2O3夹杂在DC06钢中的分布及对深冲性能的影响[J].中国冶金,2021, 31 (5): 111.
|
[3] |
上官方钦, 刘正东, 殷瑞钰.钢铁行业“碳达峰”“碳中和”实施路径研究[J].中国冶金,2021, 31 (9): 15.
|
[4] |
上官方钦, 周继程, 王海风,等. 气候变化与钢铁工业脱碳化发展[J].钢铁,2021, 56 (5): 1.
|
[5] |
马文俊, 李海波, 刘国梁,等.高等级汽车板中间包冶金技术[J].连铸,2021 (5): 99.
|
[6] |
邓小旋, 季晨曦, 王胜东, 等. 冷轧薄板线状缺陷的工艺控制[J].中国冶金,2017, 27 (4): 55.
|
[7] |
朱国森, 季晨曦, 刘洋,等.首钢板坯连铸技术进步[J].中国冶金,2019, 29 (8): 1.
|
[8] |
Zhang L,Thomas B G. State of the art in evaluation and control of steel cleanliness[J].ISIJ International,2003, 43 (3): 271.
|
[9] |
Jacobi H,Wunnenberg K.Improving oxide cleanness on basis of MIDAS method[J].Ironmaking and Steelmaking,2003, 30 (2): 130.
|
[10] |
刘新华, 蔡开科, 王兰香,等. 超低头连铸板坯非金属夹杂物研究[J].钢铁,1991, 26 (9): 25.
|
[11] |
Awajiya Y, Kubota Y,Takeuchi S. Inclusion entrapment location in solidified shell of ultra low carbon steel slab[C]//AISTech Proceedings.USA: Association for Iron and Steel Technology, 2005:65.
|
[12] |
ZHANG Q, WANG L,WANG X. Influence of casting speed variation during unsteady continuous casting on non-metallic inclusions in IF steel slabs[J].ISIJ International,2006, 46 (10): 1421.
|
[13] |
雷勋惠, 张立峰, 杨文, 等. X射线断层扫描技术在铸坯质量检测上的应用[J].中国冶金,2020, 30 (12): 44.
|
[14] |
DENG X, JI C, ZHU G, et al.Quantitative evaluations of surface cleanliness in IF steel slabs at unsteady casting[J].Metallurgical and Materials Transactions B,2019, 50(4): 1974.
|
[15] |
DENG X, JI C,CUI Y, et al. Formation and evolution of macro inclusions in IF steels during continuous casting[J].Ironmaking and Steelmaking,2017, 44 (10): 739.
|
[16] |
高帅, 王敏, 郭建龙: IF钢铸坯厚度方向夹杂物分布及洁净度评估[J].工程科学学报,2020, 42 (2): 194.
|
[17] |
Marukawa K. The challenge of braking the limit of the steel refining on the mass production[C]//19th Steelmaking Commission Reaction Process Research. Japan:Japan Society for the Promotion of Science,1996:1.
|
[18] |
Tsai H T, Sammon W J, Hazelton D E. Characterization and countermeasures for sliver defects in cold rolled products[C]//Steelmaking Conference Proceedings. Detroit: Iron and Steel Society, 1990:49.
|
[19] |
LIU Z, LI B, WU M,et al. An experimental benchmark of non-metallic inclusion distribution inside a heavy continuous-casting slab[J].Metallurgicaland Materials Transactions A,2019, 50 (3): 1370.
|
[20] |
邓小旋, 潘宏伟, 季晨曦, 等.常规低碳钢板坯的高速连铸工艺技术[J].钢铁,2019, 54 (8): 70.
|
[21] |
杨志刚, 徐子谦, 黄伟丽, 等. 连铸板坯角部纵裂原因分析及控制措施[J]. 连铸, 2021(6): 71.
|
[22] |
冯永平, 郑娜, 唐磊, 等. 薄板坯连铸结晶器内钢水凝固传热数值模拟[J]. 连铸, 2021(6): 44.
|
[23] |
王章印, 姜敏, 王新华. Q345D钢精炼过程夹杂物生成及演变行为[J]. 钢铁, 2022, 57(2): 63.
|
[24] |
杨健, 蔡文菁. 镁处理对钢中夹杂物以及HAZ组织和性能的影响[J]. 钢铁, 2021, 56(7): 13.
|
[25] |
DENG X, JI C, CUI Y,et al. Flow pattern control in continuous slab casting moulds:Physical modelling and plant trials[J].Ironmaking and Steelmaking,2017, 44 (6): 461.
|
[1] |
ZHANG Wei-feng, SHI Ru-xing, ZHANG Yan-ling, WANG Guan-bo, CHENG Guo-guang, WANG Peng-fei. Formation mechanism and improvement of detected defects in large forged Cr5 back-up roll[J]. Iron and Steel, 2022, 57(6): 91-99. |
[2] |
LIU Liang. Analysis and control over formation cause of surface longitudinal crack for continuous casting bloom of sulfur bearing steel[J]. CONTINUOUS CASTING, 2022, 41(3): 51-55. |
[3] |
ZOU Lei-lei, HUANG Jun-xiong, LI Quan-hui, ZHANG Jiang-shan, LIU Qing. Research progress on the crack and segregation prediction of continuous casting strand[J]. CONTINUOUS CASTING, 2022, 41(2): 2-9. |
[4] |
WU Xu-feng, ZHANG Cai-gui, WANG De-yong. Effect slag modification on vortex entrapment in ladle[J]. CONTINUOUS CASTING, 2022, 41(2): 41-46. |
[5] |
ZHANG Hao-hao, WU Jia-lu, LONG Mu-jun, GUO Wei, YANG Xiao-dong, CHEN Deng-fu. Evolution of micron Ti(Cx,N1-x) in TSCR process of ultra-high strength hot stamping steel[J]. CONTINUOUS CASTING, 2022, 41(2): 47-54. |
[6] |
BAI Xiao-lu, ZHANG Xiao-wei, LI Meng-fei, ZHANG Li-qiang. Corner crack controlling of niobium microalloyed steel billet for construction[J]. CONTINUOUS CASTING, 2022, 41(2): 61-65. |
|
|
|
|