Corner crack controlling of niobium microalloyed steel billet for construction |
BAI Xiao-lu1, ZHANG Xiao-wei1, LI Meng-fei2, ZHANG Li-qiang2 |
1. Steelmaking Plant,Yonggang Group Co.,Ltd.,Zhangjiagang 215628, Jiangsu, China; 2. School of Metallurgical Engineering, Anhui University of Technology, Ma'anshan 243032, Anhui, China |
|
|
Abstract In order to study the cracking of building steel containing Nb during rolling, multiple groups of low magnification samples of slab were detected and analyzed, and the chemical composition, superheat degree of tundish, drawing speed and specific water volume in secondary cooling zone were statistically analyzed combined with the production process data. The results show that the corner crack is the root of the defect, and the temperature range of niobium-containing steel slab with area shrinkage less than 75% is 750-960 ℃. By reducing the specific water volume in the first zone of the second cooling zone, appropriately increasing the specific water volume of the third zone and the fourth zone,adjusting the straightening temperature to avoid the temperature range of area shrinkage less than 75%,and a series of optimization measures to control the contents of sulfur, phosphorus and chromium so as to effective solve the corner crack defects on the slab surface and ensure the product quality of Nb containing construction steel.
|
Received: 22 January 2022
|
|
|
|
[1] |
王向松,王三忠,李靖宇,等.HP295中间裂纹产生机理分析及控制措施[J].特钢技术,2015,21(2):16.
|
[2] |
邹冰梅,阎建武,彭晓华,等.异形坯生产主要质量缺陷分析及预防[J].炼钢,2013,29(1):74.
|
[3] |
陈伟,张卫强,李金柱,等.HPB300小方坯裂纹成因分析及控制[J].炼钢,2014,30(4):10.
|
[4] |
Steven G Jansto,王厚昕.含铌钢铸坯的冶炼与连铸[J].世界钢铁,2010,10(2):17.
|
[5] |
曹建春,叶亚平,阴树标,等.铌微合金化抗震钢筋形变奥氏体连续冷却转变[J].钢铁,2019,54(12):81.
|
[6] |
郑世伟,朱立光,肖鹏程,等.低碳含铌钢铸坯裂纹形成原因分析与改进措施[J].铸造技术,2018,39(12):2759.
|
[7] |
刘志远,王重君,蔡兆镇,等.含铌微合金钢连铸坯角部裂纹控制二冷新工艺[J].中国冶金,2018,28(3):22.
|
[8] |
陆恒昌,胡春东,王存宇,等.超低碳含铌钢的块状相变及动力学[J].钢铁,2018,53(2):50.
|
[9] |
鲁献辉,马娥.连铸工艺对含铌中厚板边裂的影响[J].连铸,2015 (4):54.
|
[10] |
阴树标,刘清友,张志波,等.热变形参数对含铌钢奥氏体未再结晶区变形相变的影响[J].钢铁,2008,43(2):81.
|
[11] |
付俊岩.Nb微合金化和含铌钢的发展及技术进步[J].钢铁,2005,40(8):1.
|
[12] |
魏励,杨海滨.连铸含铌钢板坯表面横裂纹原因分析和措施[J].中国冶金,2008,18(12):17.
|
[13] |
谢仲豪,何杨,刘建华,等.大断面连铸圆坯中心裂纹的成因和控制研究[J].炼钢,2021,37(3):57.
|
[14] |
颜慧成,丁剑,王现周,等.260 t转炉底吹工艺水模试验与工业应用[J].炼钢,2020,36(2):1.
|
[15] |
陈兴华,胡志勇,朱荣,等.基于数值模拟的110 t复吹转炉氧枪优化研究[J].工业加热,2019,48(4):36.
|
[16] |
Jiang T,Hwang J Y,Mackey P J, et al. The Numerical Simulation and Application of Oxygen Lance in 120 t BOF of PANSTEEL[M]. John Wiley and Sons Inc, 2017, 44(1): 46.
|
[17] |
李彬, 马鑫, 贾睿乐, 等.连铸板坯纵裂成因及控制措施分析[J].包钢科技, 2015, 41(6):46.
|
[18] |
陈均, 刘荣蒂, 梁新腾, 等.120 t转炉氧枪喷头优化设计及工业应用[C]//第十八届(2014年)全国炼钢学术会议论文集. 西安:中国金属学会,2014.
|
[19] |
徐少禹.180 t转炉五孔氧枪的数值模拟及研究[D].鞍山:辽宁科技大学, 2014.
|
[20] |
王东兴,杨伟勇,汪春梅,等.含铌钢HRB400Nb 180 mm×180 mm铸坯角部裂纹分析及改进工艺[J].特殊钢,2020,41(5):28.
|
[21] |
杨志刚, 徐子谦, 黄伟丽, 等.连铸板坯角部纵裂原因分析及控制措施[J].连铸, 2021(1):71.
|
[22] |
靳国兵,程鹏飞,肖国华,等.矩形连铸坯角部纵裂原因分析及控制[J].河北冶金,2019(8):35.
|
[23] |
张立通,李强,段云波.连铸坯角裂缺陷产生原因及解决对策[J].包钢科技,2019,45(3):22.
|
[24] |
黄道昌,严敏,杨治争,等.45号钢厚板表面边裂原因分析与控制[J].武汉工程职业技术学院学报,2021,33(2):15.
|
[25] |
何亚元,李利巍,陆在学,等.某高强钢板拉伸断口异常原因分析[J].材料保护,2020,53(2):157.
|
[26] |
张福明,李林,刘清梅.中国钢铁产业发展与展望[J].冶金设备,2021(1):1.
|
[27] |
蔡兆镇,安家志,刘志远,等.微合金钢连铸坯角部横裂纹控制技术研发及应用[J].钢铁研究学报,2019,31(2):117.
|
[1] |
ZHANG Fu-jun, YANG Shu-feng, WANG Yong, HUANG Cheng-yong, LI Jing-sheng, YANG Jing-bo. Surface quality control of fine blanking steel slab[J]. CONTINUOUS CASTING, 2022, 41(2): 20-24. |
[2] |
LI Wei, TAN Zheng-jun, CHENG Jin-jun, LIN Qian, ZHANG Li-qiang. Quality improvement and practice of high speed continuous casting of billet based on secondary cooling optimization[J]. CONTINUOUS CASTING, 2022, 41(2): 95-99. |
[3] |
MA Fei-yue. Development and prosperity of macrostructure etching process of continuous casting billet[J]. CONTINUOUS CASTING, 2022, 41(1): 9-13. |
[4] |
DENG Yong, YANG Li-bin, WANG Cheng-yi. Application of high-speed continuous casting technology for low carbon steel slab in Masteel[J]. CONTINUOUS CASTING, 2022, 41(1): 72-77. |
[5] |
LIU Tao, CHEN Yong-feng, JIAO Kui-ming, ZHANG Hong-biao, ZUO Xiao-tan, ZHAO Li. Research on secondary cooling spray structure of billet continuous casting machine based on uniform cooling[J]. CONTINUOUS CASTING, 2021, 40(6): 91-97. |
[6] |
JIANG Dong-bin, ZHANG Li-feng, CHEN Tian-ming, LI Hong-guang, LI Jian-quan. Characterization of macrosegregation and semi-macrosegregation in continuous casting bloom[J]. CONTINUOUS CASTING, 2021, 40(4): 31-37. |
|
|
|
|