非稳态浇注对帘线钢洁净度的影响

doi:10.13228/j.boyuan.issn1005-4006.20230002

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (6182 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to have a sound grasp of the cleanliness level of tire cord steel billet produced in a steel plant under unsteady continuously casting condition, and provide the basis for determining reasonable head and tail billet length and the product classification management during industrial production, the cleanliness difference of the billet cast under unsteady and steady casting conditions was analyzed and the slag-steel interface behavior during tundish filling was studied by using water model method in the present study. The reason for the billet cleanliness difference under the two casting conditions was explained. The results show that: The cleanliness of the tire cord steel billet under the unsteady casting condition is obviously lower than that under the steady casting condition. The T.O and N is 1.76 and 1.23 times higher than that under the steady casting condition. The micro-inclusion and macro-inclusion amount of the unsteady and steady casting condition are 52.89 mm^-2 and 26.1 mm^-2, and 11.49 mg/10 kg steel and 4.36 mg/10 kg steel, respectively. Exposure of molten steel, secondary oxidation and slag entrapment during tundish filling process were found to be some reasons that lead to poor cleanliness of the billets under unsteady casting condition.

Key words： tire cord steel unsteady casting condition cleanliness of steel water model inclusions slag entrainment

Received: 05 January 2023

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	NIU Shuai
	DENG Wei
	WANG De-jiong
	HU Zhi-yong
	WANG Kai-min
	WANG Yu-hang
	TANG Hai-yan

Cite this article:

NIU Shuai,DENG Wei,WANG De-jiong等. Effect of unsteady casting condition on cleanliness of tire cord steel[J]. CONTINUOUS CASTING, 2023, 42(1): 74-81.

URL:

http://www.chinamet.cn/Jweb_lz/EN/10.13228/j.boyuan.issn1005-4006.20230002 OR http://www.chinamet.cn/Jweb_lz/EN/Y2023/V42/I1/74

[1]	赵家七, 麻晗, 王德永, 等. 碱金属氧化物对帘线钢中夹杂物的影响[J/OL]. 中国冶金, 2022.
[2]	王薛鹏, 刘荣, 王淼, 等. 高强度帘线钢 LX82A 盘条氧化铁皮的控制[J]. 河北冶金, 2022 (7):23.
[3]	孙先焦. 72A 帘线钢控冷工艺[J]. 河北冶金, 2020 (12):48.
[4]	张月鑫, 张立峰, 王举金, 等. 连铸坯全断面非金属夹杂物成分分布的预报[J]. 钢铁, 2021, 56(10):74.
[5]	李宁, 薛正良, 王璐. SWRH 92A 帘线钢中异相形核TiN复合夹杂物析出机制[J]. 钢铁研究学报, 2022, 34(10):1118.
[6]	李战卫, 沈奎, 于学森, 等. 超高强度帘线钢LX92A连续和等温冷却下的相变行为[J]. 金属热处理, 2021, 46(5):32.
[7]	李中元, 李长荣. 帘线钢中夹杂物控制技术的研究进展[J]. 热加工工艺, 2018, 47(13):6.
[8]	雷家柳, 薛正良, 朱宇航, 等. 子午线轮胎用帘线钢非金属夹杂物的研究进展[J]. 钢铁研究学报, 2018, 30(11):847.
[9]	赵昊乾, 王昆鹏, 赵铮铮, 等. 钢包初始状态对帘线钢夹杂物的影响[J]. 钢铁研究学报, 2017, 29(4):294.
[10]	陈波涛, 王凤康, 曾杰,等. 帘线钢小方坯82A铸坯表面和内部缺陷分析[J]. 连铸, 2021(6):65.
[11]	王德永, 全齐, 屈天鹏, 等. 连铸单流中间包钢液非稳态流动行为物理模拟[J]. 连铸, 2021(5):60.
[12]	储成阳, 徐宇, 武鸿杰, 等. 五流中间包稳态及非稳态试验[J]. 连铸, 2020(5):7.
[13]	李玉娣, 江中块. IF钢非稳态连铸坯洁净度分析[J]. 连铸, 2022 (2):89.
[14]	徐利平, 汪洪峰. 非稳态浇注是铸坯裂纹和夹渣的控制措施[J]. 连铸, 2019(2):27.
[15]	李慧蓉, 孙立根, 李运刚, 等. 非稳态浇注对40Mn2钢洁净度的影响[J]. 铸造技术, 2017, 38(7):1688.
[16]	孙彦辉, 蔡开科, 赵长亮. 非稳态浇注操作对连铸坯洁净度影响[J]. 钢铁, 2008, 43(1):22.
[17]	Takahashi K, Ando M, Ishii T. Numerical investigation of unsteady molten steel flow and inclusion behavior in the tundish in the ladle change period[J]. ISIJ International, 2014, 54(2):304.
[18]	Rodolfo D, Morales, Saul Garcia-Hernandez, et al. Multiphase flow modeling of slag entrainment during ladle change-over operation[J]. Metallurgical and Materials Transactions B, 2016, 47(4):2595.
[19]	肖鹏程, 朱立光, 刘海春,等. IF钢非稳态连铸坯洁净度定量分析[J]. 钢铁钒钛, 2017, 38(3):111.
[20]	马金磊, 牛帅, 唐海燕, 等. 帘线钢连铸七流中间包钢水流动特性及各流一致性研究[J/OL]. 钢铁研究学报, 2022.
[21]	刘中秋, 齐凤生, 李宝宽, 等. 板坯连铸结晶器内渣/金界面非稳态波动行为[J]. 东北大学学报(自然科学版), 2014, 35(12):1733.
[22]	周秋月, 朱坦华, 张立峰, 等. 非稳态浇铸对结晶器卷渣定量影响的大涡模拟[J]. 钢铁, 2022, 57(4):68.