Development and application of heat flux model of high casting speed billet mould |
XIANG Hongxue1,2, HAN Limin1,2, XIA Fangyong1,2, WU Guoping1,2 |
1. Metallurgical Engineering Branch,BSIET, Beijing 100043,China; 2. Beijing Metallurgy 3-D Simulation Design Engineering Technology Research Center,Beijing 100043,China |
|
|
Abstract As a key component of continuous casting equipment, mould plays a vital role in high speed continuous casting. By developing a calculation model for average heat flux of mould, the masses and heat transfer quantity of solidified shell, mushy zone area and molten steel area of control unit in mould was calculated, and then the average heat flux of mould is obtained. The accuracy of the model is verified by the actual production parameters of low casting speed and numerical simulation analysis too. Under the condition of high casting speed, the results show that for 160 mm×160 mm billet, when the effective mould length is 900 mm and the casting speed is 6 m/min, and the solidified shell thickness at the exit of the mould reaches 10 mm, the average heat flux of the mould should be 4 200 kW/m2; Taking the heat flux calculated by the model as the boundary condition, the solidification state of molten steel in the mould was simulated by finite element simulation, and the calculation results showed that the thickness of solidified shell at the exit of the mould was 10 mm. According to the heat flux obtained from the average heat flux calculation model, combined with the forced convection heat transfer model in the tube, four different mould cooling structures were designed and their convection heat transfer coefficients were calculated. Based on the calculated convective heat transfer coefficient, the heat flux of the mould for the four types of cooling structure is calculated, and then the optimal solution for high casting speed are obtained.
|
Received: 01 June 2023
|
|
|
|
[1] |
朱苗勇.高拉速连铸过程传输行为特征及关键技术探析[J].钢铁,2021,56(7):1.
|
[2] |
谢长川,李富帅,钱亮,等.高拉速小方坯铸机关键技术的研发及应用[J].炼钢,2020,36(2):59.
|
[3] |
高宇波,管蒙寒,张建斌,等.高拉速生产小方坯包晶钢表面质量控制与改善[J].炼钢,2022,38(2):49.
|
[4] |
翟冰钰,王万林,张磊.高拉速条件下中碳钢连铸用保护渣的性能研究[J].炼钢,2020,36(1):50.
|
[5] |
魏国立,朱青德,胡绍岩.MiDa超高拉速连铸结晶器保护渣初步设计[J].连铸,2020(5):16.
|
[6] |
温巨文,郭银涛,赵晓虎,等.低碳钢高拉速板坯保护渣的工业试验与应用[J].连铸,2021(2):61.
|
[7] |
王林杰,孔令种,冯亮花,等.高拉速方坯连铸结晶器钢渣界面行为特征[J].连铸,2021(4):11.
|
[8] |
李伟,谈正军,程锦君,等.基于二冷优化的高拉速方坯质量改善及实践[J].连铸,2022(2):95.
|
[9] |
徐火军.钻石结晶器的特点及应用分析[J].连铸,2001(5):16.
|
[10] |
DE LUCA A, SGRO′ A, FORNASIER M.节能:达涅利连铸机高拉速方案[C]//第九届中国国际钢铁大会.北京:中国钢铁工业协会,2016.
|
[11] |
郭春光,彭灿锋,李富帅.阳春新钢铁连铸高拉速的关键技术研究及应用[J].冶金设备,2020(5):29.
|
[12] |
谭杜,龙海山.阳春新钢铁高效铸机改造的实践[J].冶金与材料,2020,40(1):169.
|
[13] |
汪成义,崔怀周,赵斌. 180 mm×180 mm方坯连铸结晶器内流场及温度场模拟研究[C]//第十一届中国钢铁年会论文集. 北京:冶金工业出版社,2017:634.
|
[14] |
李少翔,张晓萌,李亮,等.连铸流动与凝固耦合模拟中糊状区系数的表征及影响[J].工程科学学报,2019,41(2):199.
|
[15] |
徐永斌,马春武,幸伟.用于连铸结晶器凝固传热过程热流密度的计算方法:中国,CN 102078947 A[P].2011-06-01.
|
[16] |
杨丽,柴锋,罗小兵,等.连铸结晶器内板坯传热凝固行为建模和模拟[J].连铸,2019(4):68.
|
[17] |
仇德金. 小方坯高拉速结晶器流场和温度场模拟研究[D].西安:西安建筑科技大学,2021.
|
[18] |
赵立华,苑一波,邢立东,等.电磁搅拌对特大方坯结晶器内流场及温度场影响[J].工程科学学报,2023,45(1):64.
|
[19] |
李富帅,谢长川,郭春光,等.方坯高效连铸新型结晶器传热分析与应用[J].冶金设备,2020(1):46.
|
[20] |
刘增勋,张朝阳,肖鹏程,等.冷却工艺对高速连铸结晶器传热的影响[J].钢铁,2021,56(5):41.
|
[21] |
王泽鹏,肖鹏程,朱立光,等.方坯连铸结晶器铜管温度场分析[J].钢铁,2018,53(3):38.
|
[22] |
徐旺. 冷却工艺对连铸结晶器铜壁传热的影响[D].唐山:华北理工大学,2020.
|
[23] |
陈阳,李富帅,倪赛珍,等.小方坯高拉速结晶器铜管温度的测量[J].铸造技术,2020,41(1):29.
|
[1] |
LUO Sen, ZHU Miaoyong. State of art on solidification characteristics and continuous casting process of high manganese steel[J]. Iron and Steel, 2023, 58(9): 39-58. |
[2] |
LIU Chengjun, QI Jie, JIANG Maofa. Design and application of new mold flux for high-Al steel continuous casting[J]. Iron and Steel, 2023, 58(9): 116-126. |
[3] |
LI Yaxin, LIU Yuanming, WANG Zhenhua, ZHANG Mingze, ZHANG Bowen, WANG Tao. Cross shear deformation mechanism of stainless steel/carbon steel clad plate in longitudinal corrugated rolling[J]. Iron and Steel, 2023, 58(8): 138-148. |
[4] |
KANG Yonglin, ZHU Guoming, CHEN Guijiang, QIN Zhe. Latest development of wide thin strip endless rolling technology in China[J]. Iron and Steel, 2023, 58(7): 1-8. |
[5] |
WANG Gang, GU Feixiang, QIN Jinhong, LI Junhao, PENG Zhenlong. Effect of ultrasonic surface rolling process on hydrogen permeation resistance of 18CrNiMo7-6 steel[J]. Iron and Steel, 2023, 58(7): 125-132. |
[6] |
LI Xuekai, ZHANG Yanchao, ZHANG Caijun, XIAO Pengcheng, ZHU Liguang. Influence of electromagnetic braking on metallurgical behavior in thin plate crystallization[J]. Iron and Steel, 2023, 58(6): 72-81. |
|
|
|
|