Abstract�� The cracking analysis of MnNiCu plate in cold rolling process was conducted by analyzing the microstructures, EDS and XRD. The results showed that macro��segregation generated in casting process, Mn��rich zone and Cu��rich zone were in alternative pattern and periodic fluctuation of layer distribution along plate thickness was formed after hot rolling, then cracking occurred after cold rolling.