Abstract:The causes of cracking during the process of stamping DC06 steel into automotive parts were analyzed by meansofopticalmicroscopy,X-raydiffractmeterandtensiletestingmachine.Theresultsshowedtheplasticstrainratio r of the stamping part in 45° direction was lower than the standard lower limit and the deep drawing advantage texture {111}〈110〉and{111}〈112〉wasless,leadingtothenon-uniformdeformationofthesheetandbaddeepdrawingperfor-mance.As a result,cracking first occured in the stress concentration region in the 45°direction. On this basis,the im-provementmeasureswereputforwardtostudythegenerationandvariationofthetextureinthehot-rolling,cool-rolling and recrystallization annealing process,optimize the production process,and test the improved DC06 steel sheet. The results showed that the DC06 deep drawing plate had a strong γ fiber texture,higher r-value,lower Δr,so the deep drawingperformancewasimproved.