Analysis on Fracture of Boiler Water Cooling Wall Tube |
LI Ji��Kang Wen��cheng LI |
|
|
|
Abstract The macro-appearance, microstructure and fracture appearance of a boiler water cooling wall tube, which was burst while operated in Petrochemical Corporation, were investigated, aimed to make clear the reasons for this failure event. The results show that the diameter of tube is enlarged and the tube wall becomes thin at the cracked position; the microstructure at the cracked position is the mixture of bainite and a small amount of ferrite, but the normal microstructure should be the mixture of ferrite and pearlite; the fracture surface possesses a typical feature of dimple fracture. It is considered that the fracture event was caused by instantaneous super-heat of the tube while operated.
|
Received: 21 September 2009
|
Corresponding Authors:
LI Ji��Kang
|
|
|
|
[1] |
XU Tian- han,FENG Yao- rong,WANG Dang- hui. Influence of hydrogen on mixed- mode ��/�� fracture toughness of casing- drilling steels[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 749-755. |
[2] |
HUANG Rui,WANG Huan- rong,LIU Jun- liang. Influence of coiling temperature on nano- precipitated particles of advanced nano- precipitate strengthened high strength steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 684-689. |
[3] |
YANG Ting,SU Hang,LUO Xiao-bing,CHAI Feng,ZHANG Zheng-yan. Cross section microstructure and homogeneity of mechanical properties of as quenched high strength ship steel[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 583-589. |
[4] |
LEI Dong��REN Yong��CHENG Xiao-ru��LAN Kun��QIU Jun��HUANG Da-jun. Effect of heat treatment on microstructure and mechanical properties of 316L/Q235 stainless steel composite panel[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 66-71. |
[5] |
LI Meng��SONG Xiao-jie. Reason analysis and improvement on the non-yield point of HRB400 wire rod[J]. Chinese Journal of Iron and Steel, 2017, 35(3): 7-9. |
[6] |
WANG Yu-nan. Effects of[w(Mn)]on thermal properties of Fe-Mn-C steels[J]. Chinese Journal of Iron and Steel, 2017, 52(10): 51-58. |
|
|
|
|