The texture characteristics austenitic areas hot-rolled IF steel |
|
|
|
|
Abstract By means of the X-ray orientation distribution function (ODF) the texture characteristics of the low carbon steel sheet hot-rolled in austenitic zone along the plate width and thickness direction were studied. The results showed that: the main textures in the surface, 1/4 layer and 1/2 layer of austenitic zone hot-rolled low carbon steel sheet are {110}<111> and {001}<110> texture. The textures intensity in edge of austenitic zone hot-rolled low carbon steel sheet increase clearly, because the cooling speed of the hot-rolled steel sheet at the edge is fast. The surface texture of the hot-rolled low carbon steel sheet does not change strongly along the plate width, mainly because of the smaller deformation level and the complexity of deformation and the larger temperature change. The average texture intensity in the head of austenitic zone hot-rolled low carbon steel sheet is weaker, while the average texture intensity in the tail of austenitic hot-rolled low carbon steel sheet is higher, the reason is that the relativity temperature in the tail of the austenitic hot-rolled low carbon steel sheet is lower than in the head of the austenitic zone hot-rolled low carbon steel sheet.
|
Received: 01 March 2010
|
|
|
|
[1] |
HUANG Xiang-bin,BAO Si-qian,ZHAO Gang,XU Yang,SONG Na-na,LIU Bing-bing. Primary recrystallization kinetics and texture evolution during annealing of low temperature grain-oriented silicon steel[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 577-582. |
[2] |
YIN An-min����TAO Cheng����SHU Xue-dao����SUN Bao-shou����PENG Wen-fei��. Fourth order texture coefficient detection based on the surface acoustic waves[J]. Chinese Journal of Iron and Steel, 2017, 35(5): 30-35. |
[3] |
XU Yong,,ZHAO Gang,,XIAO Huan��SU Cheng��qun,. Influence of cold reduction ratio on primary recrystallization texture of Hi��B steel[J]. Chinese Journal of Iron and Steel, 2017, 29(3): 216-220. |
[4] |
WANG Jian-gong��ZHAO Hu��XIA Yin-feng��ZHOU Xun��KANG Yong-lin��QIU Chen-yang. Development and application of ferrite rolling to Ti-IF steel in hot continuous rolling line[J]. Chinese Journal of Iron and Steel, 2017, 52(10): 65-71. |
[5] |
. Microstructures and textures of ultrafine grained D6A steel prepared using rolling and annealing[J]. Chinese Journal of Iron and Steel, 2016, 28(9): 0-0. |
[6] |
GONG Jian,,LI Jun,LI Xian-hao,WANG Xian-hui,SI Liang-ying. Microstructure evolution in grain-oriented silicon steels produced by nitriding technique[J]. Chinese Journal of Iron and Steel, 2016, 28(8): 69-72. |
|
|
|
|