A Method of Measuring the Average Pearlite Interlamellar Spacing in Steel Using Electron Probe Microanalysis |
KANG Hao1,HAN Zong-tao2,ZHAO Xian-ming3,WU Di3 |
1. School of Mechatronic Engineering, Lanzhou Jiaotong University, Lanzhou 730070, Gansu, China 2. Heibei Xinghua Steel and Iron Co., Ltd., Handan 056300, Hebei, China 3. State Key Lab of Rolling and Automation, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
Abstract Taking the typical pearlitic steel U75V as an example, a method of measuring the average pearlitic interlamellar spacing in steel by electron probe microanalysis (EPMA) was introduced. Choosing the scanning path as perpendicular to pearlite interlamellar as possible, the curve of C content alternated as ��wave trough�� and ��wave crest��. The distance between two "wave trough" or two "ware crest" is one pearlitic interlamellar spacing. The method is direct, simple, and the measurement of pearlite interlamellar spacing is close to the true value.
|
Received: 29 September 2013
Published: 17 April 2014
|
|
|
|
[1] |
WANG Zhi-chun,ZHANG Lou-cheng, YUAN Xiao-jian. Multi-frequency eddy current measurement method of continuous casting billet shell thickness[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 596-602. |
[2] |
ZOU Yu-ming��GAO Yi-fei��MA Ya-xin. Measurement of the[n-value]and[r-value]of IF steel based on the digital image correlation method[J]. Chinese Journal of Iron and Steel, 2017, 35(4): 27-32. |
[3] |
GAO Yi-fei��LIANG Xin-bang��ZHANG Hai-long��ZOU Yu-ming��LIU Ming��QI Ying-hao. Evaluation for calculating uncertainty for metallic material rotating bar bending fatigue properties[J]. Chinese Journal of Iron and Steel, 2017, 35(2): 1-6. |
[4] |
WU An-min������QIU Peng������ZHONG Han-ping������ZHANG Yan-ming����. Influence of high temperature heating furnace temperature fluctuate on creep deformation measure[J]. Chinese Journal of Iron and Steel, 2017, 35(2): 12-15. |
[5] |
TIAN Hui-xin,,LIU Yu-dong,,MENG Bo. Analysis of temperature prediction of molten steel for LF based on AdaBoost.RS[J]. Chinese Journal of Iron and Steel, 2017, 29(2): 98-104. |
[6] |
WU Wei. Measurement uncertainty evaluation of scale C Rockwell hardness test[J]. Chinese Journal of Iron and Steel, 2016, 34(4): 58-61. |
|
|
|
|