Analysis of Surface Linear Defects of Cold-Rolled Galvanized Strip |
YANG Jin-ling,PENG Qi-chun |
Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China |
|
|
Abstract Linear defect is one of the common defects of galvanized strip. The formation mechanism of linear defect is analyzed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The results indicate that Al2O3 inclusion and mold powder involve in ingot in steel-making process, resulting in scratches or rough spots on surface of cold rolled strip. Linear defects are formed at the places of scratches or cracks during hot dip galvanizing. Corresponding measures are put forward to reduce defects after comprehensive consideration of steelmaking, rolling and galvanized process.
|
Received: 21 March 2013
Published: 17 April 2014
|
|
|
|
[1] |
TIAN Ya-qiang,WANG An-dong,SONG Jin-ying,ZHENG Xiao-ping,ZHAO Ding-guo,CHEN Lian-sheng. Formation reason and control measures of surface quality defects of cold rolled steel sheet for galvanization[J]. Chinese Journal of Iron and Steel, 2017, 29(4): 312-316. |
[2] |
LUO Yan-zhao��JI Chen-xi��DENG Xiao-xuan��PAN Hong-wei��ZENG Zhi��CUI Yang. Optimization of mold flux to improve surface quality of ultra-low carbon IF steel[J]. Chinese Journal of Iron and Steel, 2017, 52(4): 38-43. |
[3] |
XIE Jie-zhi��XUN Zhong-zhong��HUANG De-zhi. Analysis of cracking on cold heading steel 10B21[J]. Chinese Journal of Iron and Steel, 2017, 42(04): 32-35. |
[4] |
REN Lei��ZHANG Li-feng��WANG Qiang-qiang��ZHAO Xing. Formation mechanism of slag rim in 304 stainless steel continuous casting mold[J]. Chinese Journal of Iron and Steel, 2016, 51(8): 35-40. |
[5] |
ZHAO Ding-guo��LI Xin��WANG Shu-huan��ZHANG Wen-xiang. Behavior of reaction and adsorption between inclusion and refractory in molten steel[J]. Chinese Journal of Iron and Steel, 2016, 51(6): 47-52. |
[6] |
LUO Yan-zhao��LIU Bai-song��YUAN Peng��GAO Pan��NI You-jin��PEI Xing-wei. Impact analysis of casting parameters on surface sliver defects for ultra-low carbon steel[J]. Chinese Journal of Iron and Steel, 2016, 41(5): 62-66. |
|
|
|
|