Microstructure and Property Control of Small Rolling Bars of GH698 Alloy |
LI Feng-yan, WANG Zhi-gang, WU Gui-lin, PAN Hui-jun |
Technical Center, Fushun Special Steel Co., Ltd.��Fushun 113001, Liaoning, China |
|
|
Abstract The problem of unqualified tensile property of small rolling bars of GH698 alloy (�ܦ�20 mm) at 750 �� was deeply investigated. The results show that for ��180 mm ingots melted with VIM+VAR, Mg content is controlled between 0.004% and 0.008%; the rolling deformation is controlled between 50% and 80%, and heating temperature is controlled between 1 140~1 180 ��, the alloy can get complete recrystallized grains of grade 2-6 after standard heat treatment, and the elevated temperature tensile property of the samples passes the initial test.
|
Received: 29 March 2013
Published: 27 June 2014
|
|
|
|
[1] |
ZHENG Gui-yun. Comparation of the high temperature tensile tests for the rolled and cast 35CrMnSi steel[J]. Chinese Journal of Iron and Steel, 2017, 35(5): 11-14. |
[2] |
XU Peng��SUN Li-jun��CHEN De-li��JI Xiao. Influence of the hot forming process on the structure of 3Cr20Ni10W2 valve steel[J]. Chinese Journal of Iron and Steel, 2017, 35(3): 21-24. |
[3] |
WU Wei. Comparison analysis of new and old national standards for metallic materials tensile test at elevated temperature[J]. Chinese Journal of Iron and Steel, 2017, 35(2): 53-58. |
[4] |
WANG Bo,,YANG Mao- sheng,ZHAO Kun- yu,YUAN Xiao- hong,. Influence of solid solution temperature on low temperature toughness of Cr- Co- Mo- Ni bearing steel[J]. Chinese Journal of Iron and Steel, 2015, 27(11): 66-72. |
[5] |
ZHANG Ping,CHEN Shi-hua,SUN Yi-qiang,WU Li-xin. Revision Statement of GB/T4335 for Determination of Ferrite Grain Size for Cold Rolled Low Carbon Sheet[J]. Chinese Journal of Iron and Steel, 2013, 31(5): 48-50. |
[6] |
LI Feng-yan,ZHAO Chang-hong,WU Gui-lin,YANG Liang,LIU Ning,CHOU Ying-yu. Effect of Rolling Process on the Microstructure and Stress Rupture Property of GH4169 Alloy Bars[J]. Chinese Journal of Iron and Steel, 2013, 31(4): 14-17. |
|
|
|
|