Effect of cooling process on microstructure and properties of low alloy abrasion resistance steel NM400 |
LIANG Liang1,2,XU De-qiang2, LIU Xu-hui2, LI Guo-cang2, DENG Xiang-tao1,HUANG Long1 |
1.State Key Laboratory of Rolling Technology and Automation,Northeastern University,Shenyang 110819,China
2.Hunan Valin Lianyuan Iron and Steel Co.,Ltd.,Loudi 417009,China |
|
|
Abstract The mechanical property and microstructure of two kinds of low alloy abrasion resistance steel plates NM400 and the evolution of the microstructure and precipitates under two cooling conditions(Front stage central cooling and Sparse cooling)were investigated byusing SANSCMT5105 electronic universal testing machine,HV9250 instrument-ed drop hammer impact testing machine,optical microscope(OM)and scanning electron microscope(SEM).The results showed that the microstructure of the two cooling processes is dominated by granular bainite.The content of bainite and the size of the precipitates in the slabs under rapid cooling conditions are relatively large.For the slow cooling,there is a certain amount of pro-eutectoid ferrite,and the size of precipitates is also small. Under the rapid cooling condition,the tensile strength of NM400 is higher,reaching 637.5 MPa,and under the slow cooling condition,the low-temperature impactenergy of NM400 at-20℃ is higher,reaching 167J.
|
|
|
|
|
[1] |
SONG Yanpei1,2,WANG Huigai2,LI Li1,SU Ming1,YOU Long2. Effect of modification treatment on microstructure and properties #br#
of wear and corrosion resistant cast iron[J]. Iron and Steel, 2019, 54(9): 106-109. |
[2] |
WANG Changshun,GUO Fujian,LI Guanglong,SHANG Chengjia. Influence of central segregation control on #br# low temperature toughness of steel[J]. Iron and Steel, 2019, 54(8): 202-208. |
[3] |
WANG Yunan,JIANG Xiaofang. Investigation on inclusions and microstructure of #br#
offshore steel for high heat input welding[J]. Iron and Steel, 2019, 54(8): 209-215. |
[4] |
YANG Geng-wei,LU Jia-wei,SUN Hui,FANG Zi-wei,ZHOU Yi-liao,YAO Nan. Microstructure, mechanical properties and phase transformation behavior of TiV microalloyed highstrength hotstrip steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 726-732. |
[5] |
LIN Peng,SUN Li-guo,MA Dang-shen,ZHOU Jian,CHI Hong-xiao. Research on high temperature behavior of microstructure and carbide in die casting 4Cr5Mo2V steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 762-769. |
[6] |
HOU Zibing,GUO Zhongao,GUO Dongwei,CAO Jianghai,CHANG Yi,WEN Guanghua. A new method for carbon content distribution based on grayscale image of casting blank macrostructure in carbon steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(7): 620-627. |
|
|
|
|