Analysis of cross striation on the surface of IFsteel |
LIU Lan-xiao1,CHEN Ling-feng2,GUAN Jian-dong1,WU Nai1,ZHOU Na1,LIU Juan1 |
1.Manufacturing Department,Beijing Shougang Co.,Ltd.,Qian'an 064400,China
2.Shougang Jingtang United Iron and Steel Co.,Ltd.,Tangshan 063200,China |
|
|
Abstract There were cross striation defects on IF steel after cold rolling,continuation annealing and pressing which seriously affected the use. After inquiry and analysis of the original chemical composition and the hot rolling process parameters of the normal and detected steel,the results showed that the chemical composition of the steel met there quirements and the hot rolling process parameters were normal. The surface fine-grains microstructure and surface carbonization were discovered on the defected sample,therefore there was a yield platform in the tensile test. Through the whole process inspection of hot rolling,cold rolling and annealing,it was found that the surface carburization was caused by a large amount of grease in the furnace wall andchamber during annealing,the sum of C and N content were as high as 80×10-6,Ti element could not convert all the C and N interstitial atoms into Ti carbonitride,so the yield platform was appeared and reslute in cross striation on the surface of the steel during pressing. Through regular cleaning of grease on furnace wall and modification of equipment such as water vapor feeding into furnace chamber,the defects of yield platform and pressing cross striation were eliminated.
|
Received: 21 December 2018
Published: 15 October 2019
|
|
|
|
[1] |
XIAO Pengcheng,ZHAO Maoguo,ZHU Liguang,HE Shengping. Mathematical simulation and experiment on #br# solidification hook of IF steel[J]. Iron and Steel, 2019, 54(7): 49-55. |
[2] |
ZHU Rui-qi,SONG Xin-li,ZHENG Ai-qin,CHEN Rong-dong,JIA Juan,FAN Li-xia. Strain hardening and microstructure characteristic of high strength IF bearing phosphorus steel[J]. Iron and Steel, 2018, 53(2): 55-59. |
[3] |
JIANG Li-mei,WANG Liang-liang. Analyzation and control of mold level fluctuation of IF steel with high P content in a slab continuous caster[J]. , 2018, 43(1): 8-12. |
[4] |
WANG Yang,CUI Heng,WANG Zheng ,YANG He. Effect of RH circulation time and holding time on cleanliness of IF steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 649-653. |
[5] |
CHEN Xiao,BAO Yan-ping,LI Ren-chun,CHEN Jun-li,LI Tai-quan,WANG Rui. Analysis of cleanliness for IF steel slabs at start of continuous casting[J]. Chinese Journal of Iron and Steel, 2017, 29(4): 281-286. |
[6] |
ZOU Yu-ming,GAO Yi-fei,MA Ya-xin. Measurement of the[n-value]and[r-value]of IF steel based on the digital image correlation method[J]. Chinese Journal of Iron and Steel, 2017, 35(4): 27-32. |
|
|
|
|