Application of the high speed drilling method of residual stress on thick wall pipeline steel pipe |
LI Rong-feng1, XU Liang2, ZHANG Shu-yan 1,3 |
1.Center of Excellence for Advanced Materials,Dongguan 523808,China
2.Pabo Testing Technology Service Co.,Ltd.,Zhuhai 519050,China
3.Songshan Lake Laboratory for Material Science,Dongguan 523808,China |
|
|
Abstract The high-speed drilling method(method A)of the standard GB/T 31310—2014 was used to determine the residual stress of JCOE SAWLwelded pipe with large wall thickness,small diameter-thickness ratio,high strength and hightoughness. The operation steps and precautions of the high-speed drilling method were introduced.The tested samples included steel plate sample,J-deformation sample,steel pipe sample before and after expansion. This method had been used to measure the residual stress of the thick wall pipeline with adepth of 1.4 mm to understand the distribution of residual stress along the surface depth. The test results showed that the residual stress state of steel pipe specimen after the mechanical expansion was well controlled,and the value was low,which was beneficial to the in-service stable operation of steel pipeline.
|
Received: 31 July 2019
Published: 15 December 2019
|
|
|
|
[1] |
CUI Jin-xing1, HAN Shi-chao2, SUN Jian-liang1, PENG Yan1. Evolution characteristics of residual stresses in medium-thick plate during thinning process[J]. Iron and Steel, 2019, 54(5): 39-46. |
[2] |
SUN Jian-liang1,2, LI Kai1, DU Xing-ming1, PENG Yan1,2. Straightening process of longitude profiled plate based on matching straightening roller system[J]. Iron and Steel, 2019, 54(3): 47-55,62. |
[3] |
CHEN Li-jun, XIE Xiao-yuan, ZHANG Juan, XIA Cai-ying, GAO Miao-miao . Performance evaluation of 12Cr1MoVG thick-wall pipe after multiple simulated post-weld heat treatment[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(3): 23-28. |
[4] |
XIONG Mao-xian, YANG Sha-sha, XIE Jun-feng, JI Bing-yin, MA Lei, SHI Jiao-qi. Discussion about correlation between blind-hole technology and the ring method in testing residual-stress of oil casing[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(3): 33-35. |
[5] |
HAN Yi1,XIAO Yao1,MIN Xiangling2,YU Enlin1,LI Dalong1,GAO Ying3. Residual stress and microstructure evolution of high #br#
frequency welding of longitudinal pipe[J]. Iron and Steel, 2019, 54(11): 130-139. |
[6] |
GAO Jingna1,2,LI Qiang1,3,GAO Ying2,LI Jianhui2,WANG Ge1. Flow and heat transfer characteristics inside gas cylinder #br#
during quenching process[J]. Iron and Steel, 2019, 54(10): 66-71. |
|
|
|
|