Cause analysis of unqualified elongation of
track shoe and improvement measures |
WEN Yongyue |
Liaoning Hongchang Heavy Industry Co., Ltd., Liaoyang 111200, China |
|
|
Guide |
|
Abstract After heat treatment of 25MnB track shoe, the sample with unqualified elongation was comprehensively analyzed. The chemical composition was detected using direct reading spectrometer. The gas composition including N, H and O was detected using oxygen-nitrogen-hydrogen analyzer. The metallographic structure and non-metallic inclusion levels were inspected using metallographic microscope. The fracture analysis of sample was conducted using scanning electron microscopy(SEM). It was found that the cooling rate of track shoe was slow in the core of grouser, leading to the formation of nonuniform structure. Moreover, the presence of ferrite led to the unqualified elongation. By changing the cooling water nozzle to increase the cooling water flow rate, the cooling rate of track shoe quenching was accelerated. Thereby the generated tempered martensite with uniform structure was formed, and the elongation of track shoe could meet the requirements of the enterprise standard.
|
Received: 15 April 2021
|
|
|
|
|
[1] |
DING Kai1,2, DONG Wufeng1,2, WANG Li3,4, PAN Hua3,4, LEI Ming3,4, GAO Yulai1,2 . Progress and challenge of liquid metal embrittlement in galvanized advanced high strength steel
[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 399-410. |
[2] |
NI Ao1, LI Chengzhi1, ZHANG Wei2, YIN Teng3, LU Zhengdong3, XUE Zhengliang2 . Numerical simulation research on tuyere air supply characteristics of large blast furnace [J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 411-420. |
[3] |
BAI Jiapei1, LIU Wenqiang1, YANG Aimin1, LI Jie1, LI Daliang2, LI Fei2 . Effect of w(MgO) on strength of pellets made of local
high silicon iron powder [J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 421-428. |
[4] |
FAN Xiaohui, ZHU Yuan, GAN Min, JI Zhiyun, SUN Zengqing, WU Yufeng . Effect of SO2 and H2O(g) in flue gas of pellet on SCR catalytic denitrification [J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 429-437. |
[5] |
ZHAO Peng1,2,ZHANG Hua1,2,FANG Qing1,2,WANG Jiahui1,2, WU Guoliang1,2,NI Hongwei1,2. Numerical study on strandblocking operation of a sixstrand square billet tundish [J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 438-450. |
[6] |
JI Junhong,JIANG Yu,DU Hongxian,WANG Shuoshuo . Numerical simulation of influence of impellers′ shape on mixing behavior by KR method desulfurization [J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 451-460. |
|
|
|
|