Defect analysis and prevention of cracking in 177.80 mm×10.36 mm P110 seamless pipe billet |
ZHANG Hailong,YUAN Xinglong |
1.NCS Testing Technology Co., Ltd., Beijing 100081, China;
2.Baoji Petroleum Steel Pipe Co., Ltd., Baoji 721008, China |
|
|
Abstract Brand 30MnCr22 177.80 mm×10.36 mm steel tube blank was converted to P110 steel tube billet after upgrading by heat treatment. Some cracks were observed on the surface of tube billet in the subsequent nondestructive testing. The crack was sampled for macrofracture analysis, metallographic analysis, fracture scanning analysis and energy spectrum analysis. The property of cracks was determined. It was found that the raw materials of tube billet contained Ti, O, Si and Al. The smelting of steel billet was not pure enough. The stress in the quenching process of heat treatment was too large to induce the formation of quenching cracks. In the process of subsequent production, the formation of such crack defects could be avoided by optimizing the steel billet smelting, selection of quenching temperature in heat treatment as well as control of cooling temperature for steel tube. Therefore, the aims to optimize process and eliminate defect could be achieved.
|
Received: 22 October 2020
|
|
|
|
[1] |
HOU Zibing1,2,LIU Qian1,2,JIANG Shaoqi1,2,PENG Zhiqiang1,2,GUO Dongwei1,2, WEN Guanghua1,2. Parameter optimization for continuous casting of lowcarbon steel based on big data mining[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(9): 952-962. |
[2] |
CHEN Shuangsheng1,2, CAO Yanguang2, YANG Gengwei1, LI Zhaodong2, DING Cancan2, LANG Tong3. Effect of quenching process on microstructure and properties of DZ2 steel for highspeed train axle[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(9): 1015-1022. |
[3] |
ZHENG Wan, KOU Jin-rong, LI Lie-jun, WANG Guan, WAN Xiang, LIU Chen-sheng. Mechanisem of reduction of subcutaneous cracking susceptibility in niobium-containing steel by nitrogen fixation with titanium microalloying[J]. Iron and Steel, 2022, 57(8): 94-102. |
[4] |
YANG Li-an, MI Jin-zhou, LI Tao, CONG Jun-qiang, DENG Ai-jun. Intelligent customization method for prediction model of longitudinal surface crack on continuously casting slab[J]. CONTINUOUS CASTING, 2022, 41(6): 16-20. |
[5] |
ZHANG He, DUAN Hai-yang, WANG Xu-dong, YAO Man. Longitudinal crack prediction method of continuous cast slab based on random forest and clustering[J]. CONTINUOUS CASTING, 2022, 41(6): 21-28. |
[6] |
HAN Zhan-guang, ZHOU Gan-shui, XIE Chang-chuan. Defect detection of billet macrostructure based on machine learning[J]. CONTINUOUS CASTING, 2022, 41(6): 38-44. |
|
|
|
|