Phosphorous Enrichment in Molten Adjusted Converter Slag: Part II Enrichment Behavior of Phosphorus in CaO-SiO2-FeOx-P2O5 Molten Slag

WANG Nan,LIANG Zhi-gang,CHEN Min,ZOU Zong-shu

钢铁研究学报(英文版) ›› 2011, Vol. 18 ›› Issue (12) : 22-26.

PDF(1946 KB)
欢迎访问《钢铁研究学报(英文版)》官方网站!今天是 2025年8月1日 星期五
PDF(1946 KB)
钢铁研究学报(英文版) ›› 2011, Vol. 18 ›› Issue (12) : 22-26.
工艺

Phosphorous Enrichment in Molten Adjusted Converter Slag: Part II Enrichment Behavior of Phosphorus in CaO-SiO2-FeOx-P2O5 Molten Slag

  • WANG Nan,LIANG Zhi-gang,CHEN Min,ZOU Zong-shu
作者信息 +

Phosphorous Enrichment in Molten Adjusted Converter Slag: Part II Enrichment Behavior of Phosphorus in CaO-SiO2-FeOx-P2O5 Molten Slag

  • WANG Nan,LIANG Zhi-gang,CHEN Min,ZOU Zong-shu
Author information +
文章历史 +

摘要

The enrichment behavior of phosphorus in CaO-SiO2-FeOx-P2O5 slag was studied by making an investigation on the distribution of phosphorous content in the CaO-SiO2-FeOx-P2O5 molten slag. The research results showed that the 2CaO·SiO2 solid particles existing in molten slag were the condensation sites for the phosphorus enrichment. The enrichment process of phosphorus in the molten slag can be recognized as three substeps: mass transfer of phosphorus from bulk slag to the surface of 2CaO·SiO2 particle, superficial solid solution reaction of phosphorus around the 2CaO·SiO2 particle, and diffusion of phosphorus through the product layer of 2CaO·SiO2-3CaO·P2O5 solid solution to the inner of 2CaO·SiO2 particle. Moreover, higher temperature is favorable to the phosphorous enrichment from molten bulk slag to the 2CaO·SiO2 particles.

Abstract

The enrichment behavior of phosphorus in CaO-SiO2-FeOx-P2O5 slag was studied by making an investigation on the distribution of phosphorous content in the CaO-SiO2-FeOx-P2O5 molten slag. The research results showed that the 2CaO·SiO2 solid particles existing in molten slag were the condensation sites for the phosphorus enrichment. The enrichment process of phosphorus in the molten slag can be recognized as three substeps: mass transfer of phosphorus from bulk slag to the surface of 2CaO·SiO2 particle, superficial solid solution reaction of phosphorus around the 2CaO·SiO2 particle, and diffusion of phosphorus through the product layer of 2CaO·SiO2-3CaO·P2O5 solid solution to the inner of 2CaO·SiO2 particle. Moreover, higher temperature is favorable to the phosphorous enrichment from molten bulk slag to the 2CaO·SiO2 particles.

图表

引用本文

导出引用
王楠, 梁志刚, 陈敏. Phosphorous Enrichment in Molten Adjusted Converter Slag: Part II Enrichment Behavior of Phosphorus in CaO-SiO2-FeOx-P2O5 Molten Slag[J]. 钢铁研究学报(英文版), 2011, 18(12): 22-26
YU Nan, LIANG Zhi-Gang, CHEN Min. Phosphorous Enrichment in Molten Adjusted Converter Slag: Part II Enrichment Behavior of Phosphorus in CaO-SiO2-FeOx-P2O5 Molten Slag[J]. Journal of Iron and Steel Research International, 2011, 18(12): 22-26

基金

和上海宝钢集团公司联合资助项目;国家自然科学基金

PDF(1946 KB)

Accesses

Citation

Detail

段落导航
相关文章

/