Non-oriented silicon steel (35W310) and amorphous ribbon (Fe78Si9B13 amorphous alloy) reactor U-cores are made by welding and dipping paint curing, respectively. Amorphous U-core used to make reactor cut sharply eddy current loss due to high electrical resistivity characteristic, thickness of thin ribbon and insulation of dipping paint. The amorphous alloy has high and constant magnetic permeability, and is more suitable for reactor design power to filter high order harmonic component. Keeping off high magnetostriction district with magnetic flux density of 50-100 mT can weaken influence on inductance of inductor due to elongation of magnetostriction. Amorphous alloy has a lower temperature rise using the software Infolytica 7. 2 simulation.

Non-oriented silicon steel (35W310) and amorphous ribbon (Fe78Si9B13 amorphous alloy) reactor U-cores are made by welding and dipping paint curing, respectively. Amorphous U-core used to make reactor cut sharply eddy current loss due to high electrical resistivity characteristic, thickness of thin ribbon and insulation of dipping paint. The amorphous alloy has high and constant magnetic permeability, and is more suitable for reactor design power to filter high order harmonic component. Keeping off high magnetostriction district with magnetic flux density of 50-100 mT can weaken influence on inductance of inductor due to elongation of magnetostriction. Amorphous alloy has a lower temperature rise using the software Infolytica 7. 2 simulation.