High temperature low cycle fatigue tests on GH4742 superalloy were studied under the total strain-controlled conditions at 650 ℃. Combined with fatigue test data, fatigue properties of the alloy were analyzed. Fracture morphology and dislocation structure were observed by scanning electron microscopy and transmission electron microscopy. The results showed that fatigue life and fatigue resistance of GH4742 alloy decreased significantly with increasing total strain amplitude. The cyclic hardening, cyclic softening and cyclic stability phenomena of the alloy occurred during the low cycle fatigue process. The increasing total strain amplitude is conducive to the formation of γ′ phase. Fatigue crack propagation is controlled jointly by ductile and brittle fracture. Inhomogeneous deformation and deformation restricted in slip bands are the main reasons for the reduction of fatigue life of GH4742 alloy.
Abstract
High temperature low cycle fatigue tests on GH4742 superalloy were studied under the total strain-controlled conditions at 650 ℃. Combined with fatigue test data, fatigue properties of the alloy were analyzed. Fracture morphology and dislocation structure were observed by scanning electron microscopy and transmission electron microscopy. The results showed that fatigue life and fatigue resistance of GH4742 alloy decreased significantly with increasing total strain amplitude. The cyclic hardening, cyclic softening and cyclic stability phenomena of the alloy occurred during the low cycle fatigue process. The increasing total strain amplitude is conducive to the formation of γ′ phase. Fatigue crack propagation is controlled jointly by ductile and brittle fracture. Inhomogeneous deformation and deformation restricted in slip bands are the main reasons for the reduction of fatigue life of GH4742 alloy.
关键词
superalloy /
low cycle fatigue /
cyclic hardening /
cyclic softening /
fracture morphology /
dislocation structure
{{custom_keyword}} /
Key words
superalloy /
low cycle fatigue /
cyclic hardening /
cyclic softening /
fracture morphology /
dislocation structure
{{custom_keyword}} /
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] HUANG Gan-yao, LI Han-kang. Superalloy [M]. Beijing: Metallurgical Industry Press, 2000:1(in Chinese).
[2] GU Yu-li, HE Yu-huai, TAO Chun-hu, et al. Low cycle fatigue fracture mechanism at elevated temperature for FGH96 nickel-base superalloy [J]. Materials engineering, 2009, (9): 56 (in Chinese).
[3] Ott M, Mughrabi H. Dependence of the high-temperature low-cycle fatigue behaviour of the monocrystalline nickel-base superalloys CMSX-4 and CMSX-6 on the γ/γ′-morphology [J]. Mater. Sci. Eng. A, 1999, 272(1): 24.
[4] Fleury E, Remy L. Low cycle fatigue damage in nickel-base superalloy single crystals at elevated temperature [J]. Mater.Sci. Eng. A, 1993, 167(1-2): 23.
[5] Shyam A, Milligan W W. Effects of deformation behavior on fatigue fracture surface morphology in a nickel-base superalloy [J]. Acta Mater, 2004, 52(6): 1503.
[6] Yue Z F, Lu Z Z. The influence of crystallographic orientation and strain rate on the high-temperature low-cyclic fatigue property of a nickel-base single-crystal superalloy [J]. Metall. Mater. Trans. A, 1998, 29 (3): 1093.
[7] Vasseur E, Remy L. High temperature low cycle fatigue and thermal-mechanical fatigue behaviour of an oxide-dispersion-strengthened nickel-base superalloy [J]. Mater. Sci. Eng. A, 1994, 184 (1): 1.
[8] Rho B S, Nam S W. The effect of applied strain range on the fatigue cracking in Nb-A286 iron-base superalloy. Mater. Lett. , 2001, 48(1): 49.
[9] Bhattacharyya A, Sastry G V S, Kutumbarao V V. The origin of microtwinning at low strains during low-cycle fatigue of Inconel 718 at room temperature [J]. J. Mater. Sci. , 1999,34 (3): 587.
[10] Lu Y L, Chen L Y, Wang G Y, et al. Hold time effects on low cycle fatigue behavior of HAYNES 230? superalloy at high temperatures [J]. Mater. Sci.Eng. A, 2005, 409 (1-2): 282.
[11] Raman S G S, Padmanabban K A. A comparison of the room-temperature behaviour of AISI 304LN stainless steel and Nimonic 90 under strain cycling [J]. Int. J. Fatigue, 1995, 17 (4): 271.
[12] Marchionmi M, Osinkolu G A, Onofrio G. High temperature low cycle fatigue behaviour of UDIMET 720 Li superalloy [J]. Int. J. Fatigue, 2002, 24 (12): 1261.
[13] Wan J S, Yue Z F. A low-cycle fatigue life model of nickel-based single crystal superalloys under multiaxial stress state [J]. Mater. Sci. Eng. A, 2005, 392 (1-2): 145.
[14] Rho B S, Nam S W, Xie X. The effect of test temperature on the intergranular cracking of Nb-A286 alloy in low cycle fatigue [J]. J. Mater. Sci., 2002, 37 (1): 203.
[15] Lord D C, Coffin L F. Low cycle fatigue hold time behavior of cast Rene 80[J]. Metall. Trans., 1973, 4: 1647.
[16] Sakaguchi M, Okazaki M. Thermo-Mechanical and Low Cycle Fatigues of Single Crystal Ni-Base Superalloys ; Importance of Microstructure for Life Prediction [J]. JSME Int. J. , 2006,49 (3): 345.
[17] Okazaki M, Sakaguchi M. Thermo-mechanical fatigue failure of a single crystal Ni-based superalloy [J]. Int. J. Fatigue, 2008, 30 (2): 318.
{{custom_fnGroup.title_cn}}
脚注
{{custom_fn.content}}
基金
Major National Science and Technology Project of High-End CNC Machine Tools and Basic Manufacturing Equipments
{{custom_fund}}