It is shown that an adapted powder sintering process can successfully prepare a 24.0%-35.5% porous titanium composite using 20 μm Ti powder and rice husk particles ranging in size between 250 μm and 600 μm. The phase constituents of the porous Ti composite samples were determined by X-ray diffraction (XRD) pattern sintered at 1250°C. The generation of silicon in the form of a TiSi2 solid solution, injected into the substrate, illustrates the solid solution strengthening effect. The average grain size of the tested sample and the grain boundary area increase along with the silicon content. This indicates that silicon is dispersed within the green compact of Ti. As the distance from a hole becomes greater, the nanohardness increases until it reaches a maximum hardness of 3.5 GPa at approximately 1.5 mm. This may be due to the solid solution strengthening of SiO2. However, nanohardness is 3.3 GPa at a distance of approximately 0.5 mm from a hole’s edge. The compressive strength is measured to be in the range of 440-938 MPa. The strain reaches 14.8%-16.6% under compression testing. A large number of cleavage steps appear following a fracture. The observed fracture is a brittle fracture. Porous Ti composites with about 36% porosity have promising potential biomaterial applications, specifically related to bone implants and biological bearings.
Abstract
It is shown that an adapted powder sintering process can successfully prepare a 24.0%-35.5% porous titanium composite using 20 μm Ti powder and rice husk particles ranging in size between 250 μm and 600 μm. The phase constituents of the porous Ti composite samples were determined by X-ray diffraction (XRD) pattern sintered at 1250°C. The generation of silicon in the form of a TiSi2 solid solution, injected into the substrate, illustrates the solid solution strengthening effect. The average grain size of the tested sample and the grain boundary area increase along with the silicon content. This indicates that silicon is dispersed within the green compact of Ti. As the distance from a hole becomes greater, the nanohardness increases until it reaches a maximum hardness of 3.5 GPa at approximately 1.5 mm. This may be due to the solid solution strengthening of SiO2. However, nanohardness is 3.3 GPa at a distance of approximately 0.5 mm from a hole’s edge. The compressive strength is measured to be in the range of 440-938 MPa. The strain reaches 14.8%-16.6% under compression testing. A large number of cleavage steps appear following a fracture. The observed fracture is a brittle fracture. Porous Ti composites with about 36% porosity have promising potential biomaterial applications, specifically related to bone implants and biological bearings.
关键词
Rice-husk, Porous Ti, sintering, Porosity, hardness, Mechanical properties
{{custom_keyword}} /
Key words
Rice-husk, Porous Ti, sintering, Porosity, hardness, Mechanical properties
{{custom_keyword}} /
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] Polmear I. Light alloys: from traditional alloys to nanocrystals. 4th ed. Burlington: Butterworth-Heinemann; 2006.
[2] Cui C, Hu B, Zhao L, Liu S. Titanium alloy production technology, market prospects and industry development. Mater Des 2011;32:1684-91.
[3] Liu Y, Chen L, Tang H, Liu CT, Liu B, Huang B. Design of powder metallurgy titanium alloys and composites. Mater Sci Eng A 2006;418:25-35.
[4] Sevilla P, Aparicio C, Planell J, Gil F. Comparison of the mechanical properties between tantalum and nickel–titanium foams implant materials for bone ingrowth applications. J Alloys Compd 2007;439:67-73.
[5] Zhao C, Zhang X, Cao P. Mechanical and electrochemical characterization of Ti– 12Mo–5Zr alloy for biomedical application. J Alloys Compd 2011;509:8235-8.
[6] Kaczmar J, Pietrzak K, W?osin′ ski W. The production and application of metal matrix composite materials. J Mater Process Technol 2000;106:58-67.
[7] Rack H, Qazi J. Titanium alloys for biomedical applications. Mater Sci Eng C 2006;26:1269-77.
[8] B. Li, F. Yan, X. Lu, Effect of microstructure on the tensile property of porous Ti produced by powder metallurgy technique, Mater. Sci. Eng. A 534 (2012) 43-52.
[9] B. Li, C. Wang, X. Lu, Effect of pore structure on the compressive property of porous Ti produced by powder metallurgy technique, Mater. Des. 50 (2013) 613-619.
[10] F. Li, J. Li, G. Xu, G. Liu, H. Kou, L. Zhou, Fabrication, pore structure and compressive behavior of anisotropic porous titanium for human trabecular bone implant applications, J. Mech. Behav. Biomed. Mater. 46 (2015)104-114.
[11] J.P. Li, S.H. Li, K. De Groot, P. Layrolle, Preparation and characterization of porous titanium, Key Eng. Mater. 218 (2001) 51-54.
[12] S.C. Cachinho, R.N. Correia, Titanium porous scaffolds from precursor powders: rheological optimization of TiH2 slurries, Powder Technol. 178 (2007)109-113.
[13] S.-W. Yook, H.-D. Jung, C.-H. Park, K.-H. Shin, Y.-H. Koh, Y. Estrin, et al., Reverse freeze casting: a new method for fabricating highly porous titanium scaffolds with aligned large pores, Acta Biomater. 8 (2012) 2401-2410.
[14] N. Jha, D. Mondal, J. Dutta Majumdar, A. Badkul, A. Jha, A. Khare, Highly porous open cell Ti-foam using NaCl as temporary space holder through powder metallurgy route, Mater. Des. 47 (2013) 810-819.
[15] H.-D. Jung, S.-W. Yook, T.-S. Jang, Y. Li, H.-E. Kim, Y.-H. Koh, Dynamic freeze casting for the production of porous titanium (Ti) scaffolds, Mater. Sci. Eng. C 33 (2013) 59-63.
[16] Y. Li, Z. GUO, J. HAO, S. REN, Porosity and mechanical properties of porous titanium fabricated by gelcasting, Rare Met. 27 (2008) 282-286.
[17] E. Carreno-Morelli, M. Rodríguez-Arbaizar, A. Amherd, J.-E. Bidaux, Porous titanium processed by powder injection moulding of titanium hydride and space holders, Powder Metall. 57 (2014) 93-96.
[18] M.-K. Ahn, I.-H. Jo, Y.-H. Koh, H.-E. Kim, Production of highly porous titanium(Ti) scaffolds by vacuum-assisted foaming of titanium hydride (TiH2) suspension, Mater. Lett. 120 (2014) 228-231.
[19] N.F. Daudt, M. Bram, A.P. Cysne Barbosa, C. Alves Jr. Surface modification of highly porous titanium by plasma treatment. Materials Letters. 141(2015)194-197.
[20] Xiao-hua WANG, Jin-shan LI, Rui HU, Hong-chao KOU. Mechanical properties and pore structure deformation behaviour of biomedical porous titanium. Trans. Nonferrous Met. Soc. China 25(2015) 1543-1550.
[21] B.Arifvianto, M.A. Leeflang, J. Zhou. The compression behaviors of titanium/carbamide powder mixtures in the preparation of biomedical titanium scaffolds with the space holder method. Powder Technology 284 (2015) 112-121.
[22] S. Mu?oz, J. Pavón, J.A. Rodríguez-Ortiz, A. Civantos , J.P. Allaind, Y. Torres. On the influence of space holder in the development of porous titanium implants: Mechanical, computational and biological evaluation. Materials Characterization 108 (2015) 68-78.
[23] GB-T 7314-2005. Metallic materials-compression testing at ambient temperature standardization. Administration of the People’s Republic of China. Beijing: Standard Press of China; 2005.
[24] B.Y. Li, L.J. Rong, Y.Y. Li, V.E. Gjunter, Synthesis of porous Ni–Ti shape-memory alloys by self-propagating high-temperature synthesis: reaction mechanism and anisotropy in pore structure, Acta Mater. 48 (2000) 3895-3904.
[25] A. Bandyopadhyay, F. Espana, V.K. Balla, S. Bose, Y. Ohgami, N.M. Davies, Influence of porosity on mechanical properties and in vivo response of Ti6Al4V implants, Acta Biomater. 6 (2010) 1640-1648.
[26] Liu B, Liu Y, He X, Tang H, Chen L, Huang B. Preparation and mechanical properties of particulate-reinforced powder metallurgy titanium matrix composites. Metall Mater Trans A2007;38:2825-31.
[27] Humphreys FJ, Hatherly M. Recrystallization and related annealing phenomena. 2nd ed. Oxford: Pergamon Press; 2004.
[28] M.A.-H. Gepreel, M. Niinomi, Biocompatibility of Ti-alloys for long-term implantation, J. Mech. Behav. Biomed. Mater. 20 (2013) 407-415.
[29] J.W. Qiao, T. Zhang, F.Q. Yang, P.K. Liaw, S. Pauly, B.S. Xu, A tensile deformation model for in-situ dendrite/metallic glass matrix composites, Sci. Rep. 3 (2013) 2816-2825.
[30] Y. Quan, F. Zhang, H. Rebl, B. Nebe, O. Ke?ler, E. Burkel, Ti6Al4V foams fabricated by spark plasma sintering with post-heat treatment, Mater. Sci. Eng. A
565 (2013) 118-125.
[31] G. Crawford, N. Chawla, K. Das, S. Bose, A. Bandyopadhyay, Microstructure and deformation behavior of biocompatible TiO2 nanotubes on titanium substrate, Acta Biomater. 3 (2007) 359-367.
[32] T. Albrektsson, C. Johansson, Osteoinduction, osteoconduction and
osseointegration, Eur. Spine. J. 10 (2001) S96-S101.
[33] M. Niinomi, Fatigue performance and cyto-toxicity of low rigidity titanium
alloy Ti–29Nb–13Ta–4.6Zr, Biomaterials 24 (2003) 2673-2683.
{{custom_fnGroup.title_cn}}
脚注
{{custom_fn.content}}
PDF(2344 KB)