Research on the first and last slab cleanness and inclusions evolved of IF steel

  • 刘 彭,罗 钢,徐刚军
Author information +
文章历史 +

摘要

分析IF钢头、尾坯离端部不同距离氧、氮含量、夹杂物评价,为头、尾坯合适的切头、切尾、如何修磨提供依据。钢水从RH出站至凝固过程中大颗粒复合夹杂物不断去除,热轧材夹杂物主要是氧化铝、氮化钛。头坯离头端2.5 m以后,尾坯离尾端1 m后,D类夹杂减少,头坯D类夹杂评级比尾坯波动大;头坯[wT[O]、][w[N]]高于中间坯18×10-6、8×10-6、尾坯[wT[O]]高于中间坯2×10-6。头坯离头端1 m后,夹杂物少于15 个/mm2,粒径4.4 μm,尾坯上离尾端1 m后,夹杂物少于10 个/mm2,粒径5.1 μm,尾坯洁净度好于头坯。

Abstract

In this paper, the analysis of oxygen, nitrogen content of IF steel’s the first and last slab at the different distance from the end, and inclusion evaluation, provided basis for the suitable cutting of the first and last slab and how to grind. Large particles of composite inclusions continue to be removed in molten steel from the RH to the solidification process. The inclusions of hot rolled plate are mainly alumina and titanium nitride. At the first slab after 2.5 m from the heat end and the last slab after 1m from the tail end, the D class inclusions reduce. The fluctuation of D class inclusions in the first slab is larger than the last slab. The[wT[O]、][w[N]]content of the first slab are 6×10-6 and 4×10-6 higher than the middle slab. The last[wT[O]]content is 1ppm higher than the middle slab. After 1m from the head of the first slab, the inclusions are less than 15/mm2, and particle size is 4.4 μm. After 1m from the end of last slab, the inclusions are less than 10/mm2, particle size is 5.1 μm. The last slab’s cleanliness is better than the first slab.

关键词

IF钢 / 夹杂物 / 头、尾坯、氧氮含量 / 洁净度

Key words

If steel / inclusion / the first last slab oxygen and nitrogen content / cleanness

图表

引用本文

导出引用
刘彭. IF钢夹杂物演变和头尾坯洁净度研究[J]. 连铸, 2017, 36(06): 36-41 https://doi.org/10.13228/j.boyuan.issn1005-4006.20170067
LIU Bang. Research on the first and last slab cleanness and inclusions evolved of IF steel[J]. Continuous Casting, 2017, 36(06): 36-41 https://doi.org/10.13228/j.boyuan.issn1005-4006.20170067

参考文献

参考文献
[1] Zhang L F Thomas B G, Wang X H, et al. Evaluation and Control of Steel Cleanness-Review. Steelmaking Conference Proceedings [C]. 2002: 431 ~452.
[2] 高文芳.冷轧薄板表而缺陷研究[J]炼钢,2006, 22(3): 22~25
[3] 张维维,李晓伟,铝春风.IF钢冷轧板表而条状缺陷[J]钢铁研究学报,2009, 21(7): 59~62
[4] Kaulmann B. Separation oI Nonmetallic Particles in Tundishes}J}. Steel Research International, 1993,64(4):203.
[5] Yogeshwar Sahai, Toshihiko Emi. Melt Flow Characterization in Continuous Casting Tundishes }J}. ISIJ International,1996,36(6):667.
[6] 洁净钢——洁净钢生产工艺技术[M]. 北京,冶金工业出版社,2019.
[7] Wang M, Bao Y P, Cui H, et al. Generation mechanism of一TiN inclusion in if steel. J Iron Steel Res, 2010, 22 29
[8] Li Z Q, Yuan L, Liu T, et al . Formation mechanism of A1203- TiN compound inclusion during IF steel solidification process. J Northeast Univ Nat Sci ,2012,33(9):1294
[9] Shi H C,Jin H C .Effect of C on the R-Value Anisotropy of Ti-Added IF Steels[J].Materials Science Forum, 2002(2):1073.
[10] 蔡开科 ,连铸坯质量控制[M].北京,冶金工业出版社,2010.

19

Accesses

0

Citation

Detail

段落导航
相关文章

/