Effect of calcium treatment on characteristics of nonmetallic #br#
inclusions in steel containing high Al
WANG Linzhu1,LI Junqi1,YANG Shufeng2,CHEN Chaoyi1,JIN Huixin1
(1. College of Materials and Metallurgy, Guizhou University, Guiyang 550025, Guizhou, China;
2. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China)
Abstract:The morphology and the composition of inclusion were observed by SEMEDS. The particle size distribution in threedimensional, the intersurface distance and the distribution of inclusions were analyzed by an image software based on the stereology method. The results indicate that there were mainly Al2O3CaO(CaS)complex inclusions and AlN inclusions in the high Al steel after the calcium treatment. As the mass percent of Ca increasing from 0.0004% to 0.0024%, the average size of inclusions decreased from 2.5 to 1.8μm, the number density of inclusions increased by about one time, and the average intersurface of inclusions decreased from 95 to 72μm. Besides, the transformation process of inclusion composition during the cooling process was studied by FactSage thermodynamic calculation and the calculated results were in agreement with the experimental results. The relationship between the nucleus size and the characteristics was analyzed based on the calculation of inclusion nucleation. The factors affecting the inclusion distribution in the steel containing high Al were also discussed.
王林珠, 李军旗, 杨树峰, 陈朝轶, 金会心. 高铝钢中钙处理对非金属夹杂物特征的影响[J]. 钢铁, 2019, 54(11): 27-32.
WANG Linzhu1,LI Junqi1,YANG Shufeng2,CHEN Chaoyi1,JIN Huixin1. Effect of calcium treatment on characteristics of nonmetallic #br#
inclusions in steel containing high Al. Iron and Steel, 2019, 54(11): 27-32.
WANG Lin-zhu, YANG Shu-feng, LI Jing-she, et al.Fatigue life improving of drill rod by inclusion control[J].High Temperature Materials and Processes, 2016, 35(7):661-668
[1]
WANG Lin-zhu, YANG Shu-feng, LI Jing-she, et al.Fatigue life improving of drill rod by inclusion control[J].High Temperature Materials and Processes, 2016, 35(7):661-668
[2]
REN Ying, ZHANG Ying, ZHANG Li-feng.A kinetic model for Ca treatment of Al-killed steels using FactSage macro processing[J].Ironmaking & Steelmaking, 2017, 44(7):497-504
[2]
REN Ying, ZHANG Ying, ZHANG Li-feng.A kinetic model for Ca treatment of Al-killed steels using FactSage macro processing[J].Ironmaking & Steelmaking, 2017, 44(7):497-504
[3]
LIND M, HOLAPPA L.Transformation of alumina inclusions by calcium treatment[J].Metallurgical and Materials Transactions B, 2010, 41(2):359-366
[3]
LIND M, HOLAPPA L.Transformation of alumina inclusions by calcium treatment[J].Metallurgical and Materials Transactions B, 2010, 41(2):359-366
[4]
TABATABAEI Y, COLEY K S, Irons G A, et al.Model of inclusion evolution during calcium treatment in the ladle furnace[J].[J]. Metallurgical and Materials Transactions B, 2018, 49(12):1-16
[5]
YANG Guang-wei, WANG Xin-hua, Huang Fu-xiang, et al.Influence of calcium addition on inclusions in LCAK steel with ultralow sulfur content[J].Metallurgical and Materials Transactions B, 2015, 46(1):145-154
[4]
TABATABAEI Y, COLEY K S, Irons G A, et al.Model of inclusion evolution during calcium treatment in the ladle furnace[J].[J]. Metallurgical and Materials Transactions B, 2018, 49(12):1-16
[5]
YANG Guang-wei, WANG Xin-hua, Huang Fu-xiang, et al.Influence of calcium addition on inclusions in LCAK steel with ultralow sulfur content[J].Metallurgical and Materials Transactions B, 2015, 46(1):145-154
[6]
VERMA N, PISTORIUS P C, Fruehan R J, et al.Calcium modification of spinel inclusions in aluminum-killed steel: reaction steps[J].Metallurgical and Materials Transactions B, 2012, 43(4):830-840
[7]
YANG G, WANG X.Inclusion evolution after calcium addition in low carbon Al-killed steel with ultra low sulfur content[J].ISIJ International, 2015, 55(1):126-133
[6]
VERMA N, PISTORIUS P C, Fruehan R J, et al.Calcium modification of spinel inclusions in aluminum-killed steel: reaction steps[J].Metallurgical and Materials Transactions B, 2012, 43(4):830-840
[7]
YANG G, WANG X.Inclusion evolution after calcium addition in low carbon Al-killed steel with ultra low sulfur content[J].ISIJ International, 2015, 55(1):126-133
[8]
ZHANG Li-feng, LIU Yang, ZHANG Ying, et al.Transient evolution of nonmetallic inclusions during calcium treatment of molten steel[J].Metallurgical and Materials Transactions B, 2018, 49(1):12-19
[9]
HU Y, CHEN W Q, HAN H B, et al.Influence of calcium treatment on cleanness and fatigue life of 60Si2MnA spring steel[J].Ironmaking & Steelmaking, 2017, 44(1):28-35
[8]
ZHANG Li-feng, LIU Yang, ZHANG Ying, et al.Transient evolution of nonmetallic inclusions during calcium treatment of molten steel[J].Metallurgical and Materials Transactions B, 2018, 49(1):12-19
[10]
VERMA N, PISTORIUS P C, FRUHAN R J, et al.Transient inclusion evolution during modification of alumina inclusions by calcium in liquid steel: Part IBackground,experimental techniques and analysis methods[J].Metallurgical and Materials Transactions B, 2011, 42(4):711-719
[9]
HU Y, CHEN W Q, HAN H B, et al.Influence of calcium treatment on cleanness and fatigue life of 60Si2MnA spring steel[J].Ironmaking & Steelmaking, 2017, 44(1):28-35
VERMA N, PISTORIUS P C, FRUHAN R J, et al.Transient inclusion evolution during modification of alumina inclusions by calcium in liquid steel: Part IBackground,experimental techniques and analysis methods[J].Metallurgical and Materials Transactions B, 2011, 42(4):711-719
WANG X, HUANG F, QIANG L I, et al.Control of stringer shaped non-metallic inclusions of CaO-Al2O3 system in API X80 linepipe steel plates[J].Steel Research International, 2014, 85(2):155-163
[13]
WANG X, HUANG F, QIANG L I, et al.Control of stringer shaped non-metallic inclusions of CaO-Al2O3 system in API X80 linepipe steel plates[J].Steel Research International, 2014, 85(2):155-163
[14]
JIANG M, WANG X, YANG D, et al.Laboratory study on prevention of CaO-containing ASTM “D-Type” inclusions in Al-deoxidized low-oxygen steel melts during basic slag refining[J].Metallurgical and Materials Transactions B, 2015, 46(6):2573-2583
[14]
JIANG M, WANG X, YANG D, et al.Laboratory study on prevention of CaO-containing ASTM “D-Type” inclusions in Al-deoxidized low-oxygen steel melts during basic slag refining[J].Metallurgical and Materials Transactions B, 2015, 46(6):2573-2583
[15]
WANG L, LI J, YANG S, et al.Nucleation and ostwald growth of particles in Fe-O-Al-Ca melt[J].Scientific reports, 2018, 8(1):1135-1143
[15]
WANG L, LI J, YANG S, et al.Nucleation and ostwald growth of particles in Fe-O-Al-Ca melt[J].Scientific reports, 2018, 8(1):1135-1143
[16]
LI T, SHIMASAKI S, TANIGUCHI S, et al.Stereological analysis of nonspherical particles in solid metal[J].Metallurgical and Materials Transactions B, 2013, 44(3):750-761
[16]
LI T, SHIMASAKI S, TANIGUCHI S, et al.Stereological analysis of nonspherical particles in solid metal[J].Metallurgical and Materials Transactions B, 2013, 44(3):750-761
[17]
WANG Lin-zhu, YANG Shu-feng, LI Jing-she, et al.Effect of Mg addition on the refinement and homogenized distribution of inclusions in steel with different Al contents[J].Metallurgical and Materials Transactions B, 2017, 48(2):805-818
[18]
王林珠.铝脱氧钢中非金属夹杂物细微弥散化的基础研究[D]. 北京: 北京科技大学, 2017.(Wang Lin-zhu. Study on the refinement and homogenized distribution of inclusions in Al killed steel[D]. Beijing: University of Science and Technology Beijing, 2017.)
[17]
WANG Lin-zhu, YANG Shu-feng, LI Jing-she, et al.Effect of Mg addition on the refinement and homogenized distribution of inclusions in steel with different Al contents[J].Metallurgical and Materials Transactions B, 2017, 48(2):805-818
[18]
王林珠.铝脱氧钢中非金属夹杂物细微弥散化的基础研究[D]. 北京: 北京科技大学, 2017.(Wang Lin-zhu. Study on the refinement and homogenized distribution of inclusions in Al killed steel[D]. Beijing: University of Science and Technology Beijing, 2017.)