Kinetics of hot metal desulfurization using CaO-SiO2-Al2O3-Na2O-TiO2 slag |
ZHANG Kang-hui,ZHANG Yan-ling,WU Tuo |
(State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China) |
|
|
Abstract Kinetic experiments of the hot metal desulfurization were carried out using the CaO-SiO2-Al2O3-Na2O-TiO2 slag at 1 673 to 1 773 K in the laboratory to study the desulfurization rate. The results indicated that the desulfurization rate was accelerated and the melting effect of slag was enhanced with the temperature increasing. The sulfur content was changeless after about 50 min for most of desulfurization reactions. A mathematical model of kinetics of hot metal desulfurization was developed to calculate the mass transfer coefficients and the mass transfer resistance of the sulfur in the molten slag during the desulfurization process. The mass transfer coefficients of sulfur were in the range of 5.02×10-7-18.69×10-7 m/s. The estimated activation energy was 464.06 kJ/mol at 1 673 to 1 723 K and 176.35 kJ/mol at 1 723 to 1 773 K. The distribution of the sulfur at the slag-metal interface was observed by the Mineral Liberation Analyzer(MLA).Combined with the image of MLA, it is finally concluded that the mass transfer of sulfur in molten slag was the restrictive step at a high temperature during the desulfurization process.
|
Received: 03 April 2018
Published: 20 November 2018
|
|
|
|
|
[1] |
Pak J J, Fruehan R J.The effect of Na2O on dephosphorization by CaO-based steelmaking slags[J].Metallurgical Transactions B, 1991, 22(1):39-
|
[1] |
Pak J J, Fruehan R J.The effect of Na2O on dephosphorization by CaO-based steelmaking slags[J].Metallurgical Transactions B, 1991, 22(1):39-
|
[2] |
Zhang Y, Li F, Wang R, et al.Application of bayer red mud-based flux in the steelmaking process[J].Steel Research International, 2017, 88(2):304-
|
[2] |
Zhang Y, Li F, Wang R, et al.Application of bayer red mud-based flux in the steelmaking process[J].Steel Research International, 2017, 88(2):304-
|
[3] |
Park J H, Min D J, Song H S.Amphoteric behavior of alumina in viscous flow and structure of CaO-SiO2(-MgO)-Al2O3 slags[J].Metallurgical and Materials Transactions B, 2004, 35(2):269-
|
[3] |
Park J H, Min D J, Song H S.Amphoteric behavior of alumina in viscous flow and structure of CaO-SiO2(-MgO)-Al2O3 slags[J].Metallurgical and Materials Transactions B, 2004, 35(2):269-
|
[4] |
Yajima K, Matsuura H, Tsukihashi F.Effect of simultaneous addition of Al2O3 and MgO on the liquidus of the CaO-SiO2-FeOx system with various oxygen partial pressures at 1573 K[J].ISIJ International, 2010, 50(2):191-
|
[4] |
Yajima K, Matsuura H, Tsukihashi F.Effect of simultaneous addition of Al2O3 and MgO on the liquidus of the CaO-SiO2-FeOx system with various oxygen partial pressures at 1573 K[J].ISIJ International, 2010, 50(2):191-
|
[5] |
Park H, Park J Y, Kim G H, et al.Effect of TiO2 on the viscosity and slag structure in blast furnace type slags[J].Steel Research International, 2012, 83(2):150-
|
[5] |
Park H, Park J Y, Kim G H, et al.Effect of TiO2 on the viscosity and slag structure in blast furnace type slags[J].Steel Research International, 2012, 83(2):150-
|
[6] |
Sohn I, Wang W, Matsuura H, et al.Influence of TiO2 on the viscous behavior of calcium silicate melts containing 17 mass% Al2O3 and 10 mass% MgO[J].ISIJ international, 2012, 52(1):158-
|
[6] |
Sohn I, Wang W, Matsuura H, et al.Influence of TiO2 on the viscous behavior of calcium silicate melts containing 17 mass% Al2O3 and 10 mass% MgO[J].ISIJ international, 2012, 52(1):158-
|
[7] |
高泽平.钢冶金学[M]. 北京:冶金工业出版社, 2016, 50.
|
[7] |
高泽平.钢冶金学[M]. 北京:冶金工业出版社, 2016, 50.
|
[8] |
GAO Ze-ping.Steel metallurgy[M]. Beijing: Metallurgical Industry Press, 2016, 50.
|
[8] |
GAO Ze-ping.Steel metallurgy[M]. Beijing: Metallurgical Industry Press, 2016, 50.
|
[9] |
吴铿, 薛向欣, 白晨光.高温冶金熔体流变特性测定方法的讨论[C]// 全国冶金物理化学学术会议.
|
[9] |
吴铿, 薛向欣, 白晨光.高温冶金熔体流变特性测定方法的讨论[C]// 全国冶金物理化学学术会议.
|
[10] |
WU Keng, XUE Xiang-xin, BAI Chen-guang.Discussion on measuring method for rheological characteristic of metallurgical melt in high temperature[C]// National symposium on physical and chemical of metallurgy.
|
[10] |
WU Keng, XUE Xiang-xin, BAI Chen-guang.Discussion on measuring method for rheological characteristic of metallurgical melt in high temperature[C]// National symposium on physical and chemical of metallurgy.
|
[11] |
韩其勇.冶金过程动力学[M]. 北京:冶金工业出版社, 1983.
|
[11] |
韩其勇.冶金过程动力学[M]. 北京:冶金工业出版社, 1983.
|
[12] |
HAN Qi-yong.Kinetics of metallurgical process[M]. Beijing: Metallurgical Industry Press, 1983.
|
[12] |
HAN Qi-yong.Kinetics of metallurgical process[M]. Beijing: Metallurgical Industry Press, 1983.
|
[13] |
Jung J K, Pak J J.A kinetic study on desulfurization of molten iron by CaO based slags[J].Journal of the Korean Institute of Metals and Materials(South Korea), 2000, 38(4):585-
|
[13] |
Jung J K, Pak J J.A kinetic study on desulfurization of molten iron by CaO based slags[J].Journal of the Korean Institute of Metals and Materials(South Korea), 2000, 38(4):585-
|
[14] |
Ja-yong C, Dae-jung K, Hae-geon L.Reaction kinetics of desulfurization of molten pig iron using CaO-SiO2-Al2O3-Na2O slag systems[J].Transactions of the Iron & Steel Institute of Japan, 2001, 41(3):216-
|
[14] |
Ja-yong C, Dae-jung K, Hae-geon L.Reaction kinetics of desulfurization of molten pig iron using CaO-SiO2-Al2O3-Na2O slag systems[J].Transactions of the Iron & Steel Institute of Japan, 2001, 41(3):216-
|
[15] |
Tong Z, Qiao J, Jiang X.Hot metal desulfurization kinetics by CaO-Al2O3-SiO2-MgO-TiO2-Na2O slags[J]. Isij International, 2016, 57(2).[J].Isij International, 2016, 57(2):245-253
|
[15] |
Tong Z, Qiao J, Jiang X.Hot metal desulfurization kinetics by CaO-Al2O3-SiO2-MgO-TiO2-Na2O slags[J]. Isij International, 2016, 57(2).[J].Isij International, 2016, 57(2):245-253
|
[1] |
BI Chuan-guang, HUANG Chun-chao, NING Xiao-jun, ZHANG Jian-liang, WANG Guang-wei, PENG Zheng-fu. Best ratio of semi-coke for blast furnace injection[J]. Iron and Steel, 2020, 55(6): 25-32. |
[2] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
[3] |
LIU Ke, HAN Yi-hua, YANG Fan, ZHU Li-guang. Effect of MgO on microstructure of CaO-Al2O3 based quaternary system mold fluxes[J]. Iron and Steel, 2020, 55(5): 52-58. |
[4] |
ZHANG Jian-liang, SUN Min-min, LI Ke-jiang, LI Hong-tao. Present situation and prospect of dissolution behavior of metallurgical coke in blast furnace hot metal[J]. Iron and Steel, 2020, 55(4): 1-11. |
[5] |
XIAO Shao-bin, WANG Wei, LIU Tian-yu, ZHANG Qin, LÜ Zhi-qing. Effects of vacancies and C atoms on mechanical properties of Fe grain boundary[J]. Iron and Steel, 2020, 55(4): 75-81. |
[6] |
ZHANG Wei-li1,WU Sheng-li1,HU Zhong-jie1,2. Statistical analysis of factors affecting desulfurization rate of activated coke for sintering flue gas[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 281-288. |
|
|
|
|