| Influence of Coiling Temperature and Total Cold Rolling Reduction Rate on Mechanical Properties of BContaining 08A1 Steel |
KANG Yonglin1,JING Qinguang1,WU Guangliang2,
WEN Dezhi2,ZHOU Chunquan 2 |
| 1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China;2. Technical Center, Hunan Hualing Lianyuan Steel Co., Ltd., Loudi 417009, Hunan, China |
|
|
|
|
Abstract Bcontaining((40～60)×106,mass fraction) and Bfree 08Al hot strips produced by CSP process were used for experiment. The hot strips were coiled at different temperatures and then cold rolled with different reduction rate. After recrystallization annealing, the formability(rvalue and nvalue) and mechanical properties (YS，TS and A) were measured by tensile tests, in addition, two kinds of annealed sheets (coiling temperature 620 ℃;75% reduction) were analyzed by Xray diffraction(ODF) and electron backscattered diffraction (EBSD). The results showed that coiling temperature and total coldrolling reduction rate have remarkable influence on the formability and mechanical properties of Bcontaining and Bfree 08A1 steels after recrystallization annealing.ODF EBSD tests showed that the fraction of γfiber texture in Bcontaining steel is lower than that in Bfree steel, nevertheless, the rotating cubic texture ({001} <110>) and Goss texture ({011} <100>) are much more than that in Bfree steel.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
| [2] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
| [3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
| [4] |
WANG Ji-hong， ZHANG Li-na， CHEN De-li， QI Yue， CAO Li-hong. Discussion about heat treatment process of X20Cr13 blade steel for gas turbine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 18-. |
| [5] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
| [6] |
YANG Yu-dan,ZHAO Hong-shan,LIU Teng-shi,DONG Han. Microstructure and properties of new high-carbon martensitic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 135-142. |
|
|
|
|
2007, Vol. 42 