Effect of Heat Treatment on Mechanical Properties of 30MnSi PC Steel Bar |
XIAO Guizhi1,DI Hongshuang1,JIA Xuejun2 |
1. The State Key Laboratory of Rolling Technology and Automation, Northeastern University, Shenyang 110004, Liaoning, China;2. Technical Center, Tangshan Iron and Steel Group Co., Ltd., Tangshan 063000, Hebei, China |
|
|
Abstract Focusing on some problems of 30MnSi prestressed concrete (PC) steel bars such as poor delayed fracture resistance, mechanical property instability, high yield ratio and so on, the tempered sorbite should be obtained by thermal refining to solve these problems and achieve excellent mechanical properties. The relationship between heat treatment parameters and tensile strength,elongation,yield ratio was obtained respectively. The effect of heat treatment parameters on microstructure, strength and ductility of the 30MnSi PC steel bars was investigated and analyzed systematically. Optimum strength and plasticity can be obtained by quenching at 920960 ℃ and tempering in the range of 390430 ℃ with constant heating time.
|
Received: 01 January 1900
|
|
|
|
[1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[2] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
[3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[4] |
WANG Ji-hong, ZHANG Li-na, CHEN De-li, QI Yue, CAO Li-hong. Discussion about heat treatment process of X20Cr13 blade steel for gas turbine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 18-. |
[5] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
[6] |
YANG Yu-dan,ZHAO Hong-shan,LIU Teng-shi,DONG Han. Microstructure and properties of new high-carbon martensitic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 135-142. |
|
|
|
|