Study on Relationship Between Precipitated Phases Containing Ti and Properties of High Strength Hot Strip |
LI Xinge1,ZHAO Zhiyi1,XUE Rundong1,YANG Xiaozhen2,XIE Jianxin1 |
1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China;2. Baoshan Iron and Steel Co., Ltd., Shanghai 200941, China |
|
|
Abstract The relationship between precipitation of Ti and mechanical properties of hot rolled high strength steel was studied by means of qualitative and quantitative tests, such as tensile test,SEM,TEM and chemical phase analysis. It was found that the strength of the coil middle part is higher than that of the outer part by about 89 MPa. The results of chemical phase analysis indicate that the percentage of precipitated Ti and the proportion of the fine carbonitride precipitates in the coil middle part are higher than that of outer part.For example, the mass percentage of fine precipitates(<60 nm) is 1.42 times higher than that of outer part. The contribution of carbonitride of Ti smaller than 10 nm to precipitation strengthing in the coil middle part is higher than that of outer part by about 38 MPa. It comes to a conclusion that the unequal Ti precipitation in different parts is the major reason that causes property nonuniformity of steel coil.
|
Received: 01 January 1900
|
|
|
|
[1] |
HE Ya-yuan,LI Li-wei,YIN Yun-yang,DENG Zhao-jun. Evolution of microstructure and properties of thickness section of wearresistant steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 512-518. |
[2] |
YE Ya-ping1,YIN Shu-biao1,4,GAO Peng1,ZHANG Yong-qing2,CHEN Wei3,CAO Jian-chun1. Effect of soaking temperature on austenitization and solid solution of niobium in antiseismic rebar[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(9): 830-836. |
[3] |
YANG Geng-wei,LU Jia-wei,SUN Hui,FANG Zi-wei,ZHOU Yi-liao,YAO Nan. Microstructure, mechanical properties and phase transformation behavior of TiV microalloyed highstrength hotstrip steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 726-732. |
[4] |
YE Ya-ping1,YIN Shu-biao1,4,GAO Peng1,ZHANG Yong-qing2,CHEN Wei3,CAO Jian-chun1. An investigation on annealing process and strengthening and toughening mechanism of 1000MPa grade microalloyed coldrolled dualphase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(10): 912-919. |
[5] |
YANG Kai. Discussion about the mechanical properties relationship between the natural cooling and 200 ℃ water cooling HRB400E[J]. , 2018, 36(3): 15-20. |
[6] |
YANG Jun,GAO Jian-hong,YANG Qi-yu. Effect of hot-rolling technology on surface chromatic aberration defects for Ti precipitation strengthened steel[J]. Iron and Steel, 2018, 53(2): 45-49. |
|
|
|
|