Application of New Ladle Slag Modifier to Refining Q345C |
PENG Jun1,WANG Shijun2,LIU Lixia2,DONG Yuanchi2,ZHOU Yun2 |
1School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China;2.School of Metallurgy and Materials, Anhui University of Technology, Ma’anshan 243002, Anhui, China |
|
|
Abstract A ladle slag modifier made from aluminum slag of making aluminum ingot or from leftover of electrolyzing Al2O3 was developed. It was applied to produce Q345C containing aluminum steel at Jinan iron and steel company. The results show that the modifier can increase the yield ratio of aluminum as well as get stable aluminum content. It can also increase desulphurizing efficiency, but not increasing the rephosphoration content while decreasing phosphorus content somewhat. There is a tendency of resilication in a permissible scope and reducing the total Fe content in slag when using the modifier. So the optimal adding content of the modifier is 80 kg/ladle according to the test.
|
Received: 01 January 1900
|
|
|
|
[1] |
LI Chen-xiao,,WANG Shu-huan,,XUE Yue-kai,,ZHAO Ding-guo,,ZHANG Ming-bo,HAN Yu. Experiment on gasification dephosphorization with coke powder reducing converter molten slag[J]. Iron and Steel, 2018, 53(9): 20-24. |
[2] |
LI Yan-long,ZHANG Li-feng,YANG Wen,WANG Lin-shu. Development of Ladle Slag Reducer Using Aluminum Dross[J]. Iron and Steel, 2014, 49(3): 17-23. |
[3] |
CHEN Jun,. Experimental on Making Slag Modifiers by Converter Dedusting Resources[J]. Iron and Steel, 2014, 49(12): 80-84. |
[4] |
PENG Qing-liang,TANG Ping,WEN Guang-hua,LIU Bing-yu,LI Ju-zhong. Slag Composition Control for the Re-Utilization of LF Hot Steel Slag[J]. Iron and Steel, 2013, 48(7): 84-88. |
[5] |
ZHANG Da-kui,YU Shu-juan,GENG Ji-shuang,HOU Hong-yu,WANG Xiang-feng. Formation and Control of Foaming Slag in Torpedo Ladle[J]. Iron and Steel, 2012, 47(11): 89-92. |
[6] |
WANG Sheng-zhao1,ZHAO Gang1 ,BAO Si-qian1,SHI Hai-ning2,DENG Shen2,ZHANG Hai-zhou3. Hot Ductility of Niobium-Microalloyed High Strength Steel Q345C Slab[J]. Iron and Steel, 2012, 47(1): 74-77. |
|
|
|
|