| Effect of Annealing of 00Cr17Ti HotRolled Band on Ridging of ColdRolled and Annealed Sheet |
| LIU Haitao1,LIU Zhenyu1,WANG Guodong1，JIANG Laizhu2 |
| 1.The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China;2.Baosteel Research Institute, Shanghai 201900, China |
|
|
|
|
Abstract Comparative experiments of 00Cr17Ti coldrolled sheets with or without hot band annealing were carried out. The effect of annealing of hot band on ridging of coldrolled and annealed sheet was investigated by microstructure and texture analysis. The results show that the coldrolled and annealed sheet with annealing of hot band exhibited slighter ridging than that without annealing, and the average roughness and maximum roughness were only 1.27 μm and 12.06 μm, respectively. The difference in ridging characteristics between these two sheets mainly derived from the difference in microstructure and microtexture. The coldrolled and annealed sheet from annealed hot band had more homogenous microstructure in normal direction (ND) and lower texture gradient in transverse direction (TD) in comparison with that without annealing of hot band. Moreover, the grain colonies of the coldrolled and annealed sheet from annealed hot band were shorter, thinner and more scattered. All that reduced ridging of the finished sheet. Thus annealing of hotrolled band is essential to improve the surface quality of finished sheet.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
LI Zhao-zhen, SONG Xin-li, LIU Jing, CHENG Zhao-yang, BI Yun-jie, JIA Juan. Effect of Cr,Mn and annealing temperature on properties of non-oriented silicon steel[J]. Iron and Steel, 2020, 55(5): 80-86. |
| [2] |
CAO Jing-hua1,PAN Hong-bo2,3,ZHANG Jing1,ZHANG Teng-fei2,LI Xu-dong2,LIU Wei-ming2,3. Continuous cooling transformation of NbTi microcarbon deep drawing dualphase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 322-328. |
| [3] |
CAI Zhen， LIANG Wen， WANG Shui-ze， LIU Yong-qian. Discussion about practice and process of ferrite rolling in Ti-IF steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 7-. |
| [4] |
YANG Geng-wei1,HU Zhuo-li1,YIN Qi-long1,MAO Xin-ping1,2,MIAO Li-sha1,LIU Yang2. Effect of phase transformation time on microstructure and mechanical properties of hotrolled TRIP steel produced by CSP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 143-149. |
| [5] |
ZHOU Liu-tao, PAN Hong-bo, PAN Shuo, WU Jie-wen. Effect of annealing process on microstructure texture and mechanical properties of 0.025C-0.326Mn steel[J]. Iron and Steel, 2020, 55(1): 93-100. |
| [6] |
FENG Lu-lu1,2,3,WU Kai-ming1,LI Ping-ping2,CHEN Shu-min2,LU Xiu-yu4,QIAO Wen-wei3. Effect of Nb on microstructure transformation in reheating process of 2000MPa bridge cable steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(1): 60-65. |
|
|
|
|
2009, Vol. 44 