Study on High Temperature Ductility of Continuously Cast Slab |
HU Mingqian1,HU Mingshan2 |
1. Steel Making Plant of Benxi Iron and Steel Corp., Benxi 117000, Liaoning, China; 2. Technology Center of Benxi Iron and Steel Corp., Benxi 117000, Liaoning, China |
|
|
Abstract The high temperature ductility of different continuously cast carbon steel slab was studied. With Gleeble2000 hot simulater to control surface cracking and improve product quality.
|
Received: 01 January 1900
|
|
|
|
[1] |
ZHOU Ren-yuan, ZHU Li-hui, LI Shi-xian, ZHAI Guo-li. Improvement of reheat-cracking susceptibility and microstructure of T23 steel[J]. Iron and Steel, 2020, 55(3): 80-86. |
[2] |
chishirong chishirongchishirong. [J]. , 2020, 45(3): 0-0. |
[3] |
. Analysis and control of slag inclusion defect of low carbon steel slab[J]. , 2020, 45(2): 0-0. |
[4] |
Gan-Shui ZHOU. Diagnosis of instability during trial production of the billet continuous casting in a steel factory in Vietnam[J]. , 2020, 45(2): 0-0. |
[5] |
LAN Peng, TIE Zhan-peng, ZHANG Wei, MIAO Hong-sheng, YAN Qing-zhong, ZHANG Jia-quan. Research progress on spot segregation defects in continuously cast semi-products[J]. Iron and Steel, 2020, 55(2): 11-22. |
[6] |
DUAN He, SHAN Yi-yin, YANG Ke, SHI Xian-bo, YAN Wei, REN Yi. Experimental on process, microstructure and mechanical properties of X80 high strength pipeline steel for low temperature[J]. Iron and Steel, 2020, 55(2): 103-111. |
|
|
|
|