| Quantitative Texture Analysis of Cold Drawn Pearlitic Steel Wires |
| YAO Xusheng,LIU Yandong,ZUO Liang |
| Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang 110004, Liaoning, China |
|
|
|
|
Abstract Texture of cold drawn pearlitic steel wire was investigated by a method combining modified texture measurement method with orientation distribution function (ODF). The wire was austenited at 1223 K for 0.5 h, then isothermally treated at 296, 773 and 923 K for 0.5 h before cold drawing.The results showed that the <110> fibre texture is mainly gathered on the αfibre in cold drawn wire.The main texture components are {001}<110>, {111}<110> and {110}<110>，and the component {001}<110> is the strongest. Results of quantitative calculation showed that <110> component tends to increase from surface to center at 296 K; The <110>component first increases then decreases from surface to center at 773 and 923 K and has the highest value in the center at 923 K.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
LI Zhao-zhen, SONG Xin-li, LIU Jing, CHENG Zhao-yang, BI Yun-jie, JIA Juan. Effect of Cr,Mn and annealing temperature on properties of non-oriented silicon steel[J]. Iron and Steel, 2020, 55(5): 80-86. |
| [2] |
CAI Zhen， LIANG Wen， WANG Shui-ze， LIU Yong-qian. Discussion about practice and process of ferrite rolling in Ti-IF steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 7-. |
| [3] |
ZHOU Liu-tao, PAN Hong-bo, PAN Shuo, WU Jie-wen. Effect of annealing process on microstructure texture and mechanical properties of 0.025C-0.326Mn steel[J]. Iron and Steel, 2020, 55(1): 93-100. |
| [4] |
ZHANG Jian-jun，KOU Sha-sha，LI Wen-ya. CauseanalysisofDC06deepdrawingcrack[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(5): 47-50. |
| [5] |
LI Cheng- gang,ZHANG Yuan- xiang,WANG Yang,FANG Feng,CAO Guang- ming. Study on secondary recrystallization of Goss grains in strip- cast grain- oriented electrical steels[J]. , 2019, 31(2): 202-206. |
| [6] |
CHENG Si- fei,JIAO Hai- tao,XU Yun- bo. Microstructure evolution during deformation and heat treatment of strip- cast oriented Fe- 6. 5%Si steel[J]. , 2019, 31(2): 233-238. |
|
|
|
|
2008, Vol. 43 